Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 283 MPa @Thickness 9.50 - 25.4 mm, Temperature 538 °C |
41000 psi @Thickness 0.374 - 1.00 in, Temperature 1000 °F |
0.2% offset |
Haynes Hastelloy® S alloy, flat products Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Tensile Strength, Yield | 283 MPa @Thickness 3.20 mm, Temperature 316 °C |
41000 psi @Thickness 0.126 in, Temperature 601 °F |
0.2% Offset |
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Sheet, Cold Rolled and Solution Annealed HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
Tensile Strength, Yield | 283 MPa @Strain 0.200 %, Temperature 21.1 °C |
41000 psi @Strain 0.200 %, Temperature 70.0 °F |
Annealed, Transverse Orientation |
AK Steel 439 ULTRA FORM® Stainless Steel AK Steel 439 ULTRA FORM™ was developed for applications requiring oxidation and corrosion resistance superior to Type 409 as well as superior formability to AK Steel 439 Stainless Steel. As a resul.. |
|||
Tensile Strength, Yield | 283 MPa @Strain 0.200 %, Temperature 204 °C |
41000 psi @Strain 0.200 %, Temperature 399 °F |
|
Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C) Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |