Polymer Property : Tensile Strength, Yield = 496 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	496 MPa @Temperature 71.1 °C	72000 psi @Temperature 160 °F	0° Direction, Dry; ASTM D638
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 4581 Quartz Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle..
Tensile Strength, Yield	496 MPa @Temperature 71.1 °C	72000 psi @Temperature 160 °F	0° Direction, Wet; ASTM D638
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 4581 Quartz Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle..
Tensile Strength, Yield	496 MPa @Thickness 1.57 mm	72000 psi @Thickness 0.0620 in	LW; ASTM D638
Industrial Laminates/Norplex NP545 Carbon Fiber (discontinued **) Description: NP545 is composed of carbon fiber fabric and an epoxy resin system. It has excellent moisture resistance and physical properties. Potential uses include fixtures and gage systems, high ..
Tensile Strength, Yield	496 MPa @Temperature 871 Â°C, Time 45700 sec	71900 psi @Temperature 1600 Â°F, Time 12.7 hour	As Welded, Solution Annealed, and Aged; Weld/Weld Fracture; 0.2% Offset
Haynes 282Â® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Tensile Strength, Yield	496 MPa @Temperature 23.0 °C	72000 psi @Temperature 73.4 °F
ATI Wah Chang TI-3Al-2.5V Ti-3Al-2.5V has proved to be a sufficiently malleable material for tube manufacture. It can be cold worked by standard tube making processes, is weldable and can be strength-ended by cold working an..