Polymer Property : Tensile Strength, Yield = 495 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	495 MPa @Diameter 12.7 mm, Temperature 25.0 Â°C	71800 psi @Diameter 0.500 in, Temperature 77.0 Â°F	0.2% offset
Haynes HastelloyÂ® C-2000Â® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..
Tensile Strength, Yield	495 MPa @Strain 0.200 %, Temperature 200 Â°C	71800 psi @Strain 0.200 %, Temperature 392 Â°F	Bar
Special Metals INCONELÂ® alloy MA758 Ni-Cr Superalloy INCONELÂ® alloy MA 758 is an oxide-dispersion-strengthened (ODS) nickel-chromium superalloy, made by mechanical alloying. It is a development of the well-established aerospace superalloy, INCONEL..
Tensile Strength, Yield	495 MPa @Strain 0.200 %, Thickness 7.90 - 25.0 mm	71800 psi @Strain 0.200 %, Thickness 0.311 - 0.984 in	Typical Strength
Constellium Certal® Thick Aluminum Plate Certal® thick plates have been optimized to provide excellent machinability, shape stability and high strength. Certal® is therefore ideal for industrial tools. Applications include injection and ..
Tensile Strength, Yield	495 MPa @Strain 0.200 %, Thickness 25.0 - 100 mm	71800 psi @Strain 0.200 %, Thickness 0.984 - 3.94 in	Typical Strength
Constellium Certal® Thick Aluminum Plate Certal® thick plates have been optimized to provide excellent machinability, shape stability and high strength. Certal® is therefore ideal for industrial tools. Applications include injection and ..
Tensile Strength, Yield	>= 495 MPa @Strain 0.200 %	>= 71800 psi @Strain 0.200 %	Minimum
Aleris Hokotol Aluminum Alloy, 100 mm Thickness Sample treatment not specified for property data.Applications include molds for blow forming and injection molding for plastics; bolsters and force plates; high strength/low weight machine parts; an..