Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 301 MPa @Thickness 12.7 mm, Temperature 538 °C |
43700 psi @Thickness 0.500 in, Temperature 1000 °F |
0.2% offset |
Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
Tensile Strength, Yield | 301 MPa @Thickness 9.50 mm, Temperature 204 °C |
43700 psi @Thickness 0.374 in, Temperature 399 °F |
0.2% offset |
Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
Tensile Strength, Yield | 301 MPa @Thickness 12.7 mm, Temperature 93.0 °C |
43700 psi @Thickness 0.500 in, Temperature 199 °F |
0.2% offset |
Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
Tensile Strength, Yield | 301 MPa @Temperature 23.0 °C |
43700 psi @Temperature 73.4 °F |
|
ATI Allegheny Ludlum Stainless Steel Type 201, Annealed (UNS S20100) Allegheny Ludlum Type 201 and 201L have the greatest tonnage of the Cr-Ni-Mn steels (200 series). Type 201 provides advantages over the 18-8 grades in certain applications. Lower cost manganese an.. |