Polymer Property : Tensile Strength at Break = 3130 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	21.6 MPa	3130 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ HC 2190G Polyvinyl Chloride, Flexible (PVC, Flexible) Geon HC 2190G is a 90 Shore A non-phthalate, gamma-stable flexible vinyl compound made from FDA sanctioned ingredients. HC 2190G can be used for extrusion and injection molding healthcare applicatio..
Tensile Strength at Break	21.6 MPa @Thickness 2.00 mm	3130 psi @Thickness 0.0787 in	50mm/min; ASTM D638
LG Chemical KEYFLEX BT 1030D Ester Type TPE Description: Injection Molding, TPC-ET, General Purpose, Low ModulusApplication: Automotive Interior, Soft Touch GripsCAS: 37282-12-5Information provided by LG Chemical
Tensile Strength at Break	21.6 MPa	3130 psi
LG Chemical LGflex EBNW Plasticizer Features: Excellent Adhesion, Transparency, and Non-endocrine disrupterApplication: PVC Food Package WrapInformation provided by LG Chemical
Tensile Strength at Break	21.6 MPa	3130 psi	ASTM D638
Lotte Chemical Titan TITANZEXÂ® HI2000 High density polyethylene HI2000 is a high density polyethylene for injection molding. HI2000 meets the U.S. Food and Drug Administration (FDA) criteria for food contact use as specified in 21 CFR 177.1520 (c) 3.1a & 3.2a. A..
Tensile Strength at Break	21.6 MPa	3130 psi	ASTM D638
Solvay Specialty Polymers PolidanÂ® EC/110 Polyethylene, Crosslinked (XLPE) PolidanÂ® XLPE-PEX -Cross-linkable Polyethylene. Low density polyethylene based compound crosslinkable by moisture; it consists of a silane pregrafted base compound (SioplasÂ® method) to be use..
Tensile Strength at Break	21.6 MPa @Temperature 200 Â°C, Time 252000 sec	3130 psi @Temperature 392 Â°F, Time 70.0 hour	After Dry Heat Aging; ASTM D865
Seals Eastern 7182B Fluorocarbon-Elastomer Formulated AFLASÂ® high-temperature, high-pressure "sour" oil & gas service. ED resistant. Excellent acid and base resistance.Information provided by Seals Eastern, Inc.
Tensile Strength at Break	21.6 MPa	3130 psi	50 mm/min; ASTM D638
Supreme Petrochem SH 03 High Impact Polystyrene Characteristics High flow Good melt strength Excellent toughness Processing MoldingApplications Gas assisted injection molding of T.V. cabinets Suitable for thin walled parts, AC grills and toys ..
Tensile Strength at Break	21.6 MPa	3130 psi	50 mm/min; ASTM D638
Supreme Petrochem SP 8001 High Gloss, ESCR High Impact Polystyrene Characteristics Very high toughness Excellent ESCR properties against common food chemicals High gloss & heat resistance Processing Extrusion & Forming Applications Fatty food containers Co-extru..