- Polymer Property : Tensile Strength at Break = 2200 psi
Polymer Property : Tensile Strength at Break = 2200 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 15.2 MPa | 2200 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible Y126 White 317 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable JJX20A Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable JLC31A Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable W2403 Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible R132BE Polyvinyl Chloride + NBR (PVC+NBR) Information provided by PolyOne |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible R208AE Polyvinyl Chloride + NBR (PVC+NBR) Information provided by PolyOne |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible R8570A Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible 83700 Polyvinyl Chloride, Flexible (PVC, Flexible) Automotive OEM approval(s).Information provided by PolyOne |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible B80MB Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D638 |
| LyondellBasell Petrothene® GA808091 Linear Low Density Polyethylene ApplicationsPETROTHENE GA 808-091 is a broad molecular weight, linear low density polyethylene resin designed for use as a base resin in wire and cable jacketing. An antioxidant package is added to.. |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D638 |
| LyondellBasell Petrothene® NA324009 Low Density Polyethylene (Blow Molding Applications) ApplicationsPETROTHENE NA 324-009 is a low density homopolymer resin intended for blow molding applications. NA 324-009 provides good clarity, toughness and processability. Typical applications in.. |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D1414 |
| Greene Tweed CHEMRAZ® E38 Perfluoroelastomer Chemraz® E38 was specifically developed for high-density plasma systems and diffusion processes where seal reliability and very minimal contamination are essential. The material provides excelle.. |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | |
| Taiwan PU Corporation CPU-69-A/B Mixing Ratio 100/42 Polyurethane Casting Elastomer Compound of CPU-69-A/B with a mixing ratio of 100/42.Information provided by Taiwan PU Corporation.MatWeb has a separate entry for the unmixed A nd B components. |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | ISO R 527 |
| Stir SpA AF 89 CZ (PVC) Application: Extrusion flame resistant sheath CEI 20-11 type R 2Information provided by STIR SpA |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D638 |
| Teknor Apex APEX® 157-V Polyvinyl Chloride, Flexible Notes: 105°C Jacket; RoHS Compliant Features: Low to no Migration; Oil Resistant; Good UV Resistance; Sunlight Resistant (720 hours) Uses: Flexible Cord Jacketing; Wire and Cable ApplicationsForm.. |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D638 |
| Teknor Apex APEX® 3310-80NT Polyvinyl Chloride, Flexible Features: DEHP Plasticizer; Ethylene Oxide Sterilizable Uses: Food Service Applications; Medical/Healthcare Applications; Tubing Processing Forms: Extrusion Forms: PelletsInformation Provided by Tek.. |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D638 |
| Teknor Apex Fireguard® 910L16-C6-NL1 Polyvinyl Chloride, Flexible Notes: RoHS Compliant Features: Flame Retardant; Low Smoke Emission Uses: Plenum Cable Jacketing Wire Types: CL2P; CL3P; CMP; FPLP; MPP; OFNP Agency Ratings: NEC Article 725; NEC Article 760; NEC Ar.. |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D412 |
| Teknor Apex MF 569 Polyvinyl Chloride, Flexible Film Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Film, Medical Applications Forms-PelletsInformation provided by Teknor Apex Company |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D638 |
| Teknor Apex APEX® 03-A0673C-85 Polyvinyl Chloride, Flexible Notes: 75°C Jacket; RoHS CompliantFeatures: Low Temperature Flexibility Uses: Wire Jacketing; Wire and Cable Applications Agency Ratings: UL 719Forms: Pellets Wire Types: NMB; NMProcessing Method.. |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D412 |
| Teknor Apex Telcar® TL-88-N809C Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets P.. |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D412 |
| Teknor Apex Uniprene® UN-2678C Thermoplastic Vulcanizate Notes: Injection Rate: Fast Uses: Expansion Joint; Grommets; Tubing; Gaskets; Plugs; Weatherstripping; Glazing; Shock Absorbing Pads Forms: Pellets Processing Method: Extrusion; Injection Molding Ex.. |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
| 3M Dyneon™ FLS 2530 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FLS 2530 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu.. |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D412 |
| Teknor Apex Monprene® MP-1878 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | Across Flow; ASTM D412 |
| ExxonMobil Santoprene® 221-87 Thermoplastic Elastomer
(discontinued **) A hard, colorable, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide.. |
|||
| Tensile Strength at Break | 15.2 MPa | 2200 psi | TM R050-36 |
| Resinlab® EP1305 Black Highly Toughened Urethane Modified Epoxy Resinlab™ EP1305 Black is a highly toughened urethane modified epoxy designed for bonding PVC, metals, ceramics and other difficult to bond substrates. The system has a thixotropic non-sag viscosi.. |
|||