Polymer Property : Tensile Strength at Break = 2010 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	13.9 MPa @Temperature 200 Â°C, Time 360000 sec	2010 psi @Temperature 392 Â°F, Time 100 hour	After Dry Heat Aging; ASTM D865
Seals Eastern 7130 Fluorocarbon-Elastomer FKM specially for oil & gas service.Information provided by Seals Eastern, Inc.
Tensile Strength at Break	13.9 MPa	2010 psi	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
3M Dyneon™ FC 2110Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2110Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu..