Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 10.3 MPa | 1500 psi | 2 in/min; ASTM D638 |
RheTech Products E206-01 Linear Low Density Polyethylene, Black Applications: Flexible componentsConsumer GoodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | >= 10.3 MPa | >= 1500 psi | ASTM D638 |
S&E Specialty Polymers GPP1001M-P-2986 Grey PP Application: High impact resistance, non-blooming flame retardant polypropylene compound for UL94-V0 injection molding applications.Information provided by S&E Specialty Polymers |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D638 |
LyondellBasell Petrothene® GA574189 Linear Low Density Polyethylene, Injection Molding Grade PETROTHENE GA574189 exhibits excellent flow and impact with good stiffness. Typical applications include lids, closures, containers, housewares and medical items.Regulatory Status: GA574189 meets th.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D638 |
LyondellBasell Petrothene® NA205000 Low Density Polyethylene, Extrusion Coating Grade Petrothene NA205000 is an extrusion coating resin especially recommended for high-speed, light weight coating applications. The resin can be drawn to a low coating weight at line speeds in excess of.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D1414 |
Greene Tweed CHEMRAZ® 522 Perfluoroelastomer Chemraz®, a proprietary Greene, Tweed compound, has the broadest chemical resistance of any elastomeric material. Chemraz combines the resilience and sealing force of an elastomer with chemical r.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D412 |
Multibase Multi-Flex® A 7011 TPE Thermoplastic Elastomer This material bonds to polypropylene.Forms:PelletsProcessing Method:Injection Molding Information provided by Multibase |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | |
Shin-Etsu Silicones SV-13500U Silicone Rubber SV13500U is one of a series of easy processing, general purpose silicone rubber bases. It can be used in a variety of applications requiring finishing by molding, extruding or calendaring. Product F.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | DBPH Cure |
Shin-Etsu Silicones SV-16000U Silicone Rubber SV16000U is one of a series of easy processing, no post cure silicone rubber bases. It can be used in a variety of applications requiring finishing by molding, extruding or calendering. Product Feat.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | |
Shin-Etsu Silicones SV-56000U High Strength Silicone Elastomer SV56000U is one of a series of silicone bases designed for applications requiring high strength. Product Features: Excellent mechanical properties.Typical Applications: Molding and Extrusion applica.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D412 |
Teknor Apex Monprene® MP-1561 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D412 |
Teknor Apex Monprene® MP-1671 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D412 |
Teknor Apex Monprene® MP-2215 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D638 |
Teknor Apex APEX® 1001 Polyvinyl Chloride, Flexible Notes: 60°C General Purpose; RoHS Compliant Uses: Connectors; Grommets; Plugs; Strain ReliefsForms: Pellets Processing Method: Injection Molding Agency Ratings: UL QMFZ2 .E54709 Wire Types: Molde.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D412 |
Teknor Apex Monprene® MP-2455 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D412 |
Teknor Apex Monprene® MP-2955 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D412 |
Teknor Apex Telcar® TL-1654A Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D412 |
Teknor Apex Telcar® TL-3260R Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D412 |
Teknor Apex Telcar® TL-2519F Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D638 |
ExxonMobil Escorene® LD 713.93 Molding, extrusion and compounding resin Escorene Ultra LD 713.93 is a 14.4 wt% vinyl acetate copolymer with very good toughness, high clarity and excellent processability. It is suitable for use in making molded articles, extruded profile.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D638 |
ExxonMobil LLDPE LL 4004EL Wire & Cable Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 4004EL is a C4 Ziegler Natta LLDPE, especially designed for Low Voltage power cable insulation, using the two-step silane cross-linking process. Sufficient Cu-inhibitor shoul.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | Compression molded; ASTM D638 |
Dow 620I Linear Low Density Polyethylene (LDPE) For extruded foam applications Complies with U.S. FDA 21 CFR 177.1520 (c) 2.1 Information provided by Dow |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D412 |
Teknor Apex Monprene® MP-2357-L3 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D638 |
ExxonMobil LD 419.MV Wire & Cable Resin
(discontinued **) LD 419.MV is a LDPE designed for wire and cable applications and is suitable for making crosslinkable compounds for medium voltage insulation.Information provided by ExxonMobil Chemical |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D638 |
Aaron Industries AVPE LD 300-1 MELT 20 Virgin Polyethylene A natural, high flow Low Density Polyethylene resin, specifically designed for high speed injection molding applications. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | TM R050-36 |
Resinlab® EP1282 Clear Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP1282 Clear is a two part unfilled electronic grade epoxy encapsulant designed for medium sized castings. It is recognized under the Component Recognition Program of Underwriters Laborat.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | TM R050-36 |
Resinlab® EP1282 Black Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP1282 Black is a two part unfilled electronic grade epoxy encapsulant designed for medium sized castings. It is recognized under the Component Recognition Program of Underwriters Laborat.. |