Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 9.00 MPa | 1310 psi | ISO 527 |
Polimeri Europa Clearflex® MQ F0 Very Low Density Polyethylene Clearflex MQ F0 is a linear polyethylene, with antioxidants, characterized by a very low density (VLDPE).The resin shows an excellent balance between flexibility and impact resistance.Main Applicati.. |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | 500 mm/min; ASTM D638 |
Eastman E6838-913P Polyethylene
(discontinued **) Polyethylene E6838-913P natural is a specialty formulation suggested for high-speed extrusion coating applications. E6838-913P offers improvements over standard low-density polyethylene in adhesion .. |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCD933 PPE-TPE Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as insulation of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN.. |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCP921A PPE-TPE (Asia Pacific) Flexible Noryl* injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for overmolding applications such as plugs, strain reliefs, and connect.. |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP PDXF89080 PE LNP* LUBRICOMP* PDXF89080 is a compound based on Polyethylene containing Proprietary Fillers. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCD933 PPE-TPE (Europe-Africa-Middle East) Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as insulation of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN.. |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | 500 mm/min; ASTM D638 - ISO 527-2 |
DuPont Elvaloy® 3427 AC Ethylene and 27% Butyl Acrylate Copolymer Elvaloy® 3427 AC can be used for coextrusion and compounding. It can also be used in extrusion coating. Elvaloy® 3427 AC is very soft and flexible, and has good adhesion to various polymers. It.. |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | 500mm/min; ASTM D638 Type IV Specimen |
Westlake EC4042AA Low Density Polyethylene WESTLAKE low-density polyethylene EC4042 is a low density resin designed for applications, such as sugar pouches and freezer wrap, where high coating speeds and good drawdown are required. The combi.. |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | 500mm/min; ASTM D638 Type IV Specimen |
Westlake EC811AA Low Density Polyethylene WESTLAKE low-density polyethylene EC811 is used for extrusion coating applications. It exhibits good adhesion, low coat weight, and fast heat seals.Application/UsesCoatings for paper/paperboardFDA: .. |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | ASTM D638 |
ELASTO UK Dryflex® 600800S SEBS Based Material, Filled Qualities, 80A Hardness, Natural The most significant features of the 600-series are the improved heat stability, the sound reduction and that the material enables an easy and secure pigmenting for the customer. A filled material .. |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | ASTM D638 |
ELASTO UK Dryflex® 662800S SEBS Based Material, Semi-Filled Qualities, 80A Hardness, Black The 660-series is recommended when the properties of the produced detail requires the advantages of the 500-series in combination with the 600-series. A semi-filled material can therefore combine t.. |
|||
Tensile Strength at Break | 9.03 MPa | 1310 psi | Across Flow; ASTM D412 |
ExxonMobil Santoprene® 8221-85M300 Thermoplastic Elastomer A hard, colorable, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material is designed for automotive interior applications requiring low fogging and .. |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | ISO R 527 |
Fainplast Compounds GS 55 Flexible PVC, Injection Molding for Footwear Tennis shoes |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | ISO R 527 |
Fainplast Compounds GS 55/AT Flexible PVC, Injection Molding for Transparent Technical Items Toys |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | ISO R 527 |
Fainplast Compounds GSK 61 Flexible PVC, Injection Molding, Lead Free Items for building industry |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | ISO 527-1/-2 |
DuPont Performance Polymers Hytrel® HTR8351 NC021 Polyester Elastomer TPC-ET
(Unverified Data**) 30 Shore D Easy-to-Strip UV Stabilized Polyester Elastomer with Non-discoloring Stabilizer Developed for Extrusion Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | ASTM D638 |
Arkema Group EVATANE® 33-45 Copolymer Ethylene - Vinyl Acetate EVATANE® 33-45 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. EVATANE® 33-45 is stabilized with antioxidants. The High Vinyl Acetate co.. |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | ASTM D638 |
Azdel SuperLite® SL551200-100 PP Resin Matrix / 55% Glass Fiber (6 mm Molded Thickness) AZDEL SuperLite® SL551200-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 9.00 MPa | 1310 psi | ISO R 527 |
Fainplast Compounds PMP 60 Flexible PVC, Extrusion Modified with PU Various profiles |
|||
Tensile Strength at Break | >= 9.00 MPa | >= 1310 psi | |
Beijing Evergrow Resources PTFE, 24% Bronze, 12% Glass Fiber, 6% Graphite Filled Filled PTFE article is manufactured by molding method with filled PTFE resin. Filled PTFE resin is manufactured by compounding PTFE granular resin with filler. Broadly speaking PTFE compounds have t.. |