Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 9.40 MPa | 1360 psi | ASTM D412 |
DuPont Elvax® 40L-03 High Temperature Ignition Cable Jacket Formulation
(discontinued **) Elvax® 40L-03 high temperature ignition cable jacket.Information provided by DuPont. |
|||
Tensile Strength at Break | 9.40 MPa | 1360 psi | After 7 days/150°C air oven, ASTM D573 |
DuPont Elvax® 40L-03 High Temperature Ignition Cable Jacket Formulation
(discontinued **) Elvax® 40L-03 high temperature ignition cable jacket.Information provided by DuPont. |
|||
Tensile Strength at Break | 9.40 MPa | 1360 psi | ASTM D412 |
DuPont Elvax® 40L-08 High Temperature Ignition Cable Jacket Formulation
(discontinued **) Elvax® 40L-08 high temperature ignition cable jacket.Information provided by DuPont. |
|||
Tensile Strength at Break | 9.40 MPa | 1360 psi | After 7 days/150°C air oven, ASTM D573 |
DuPont Elvax® 40L-08 High Temperature Ignition Cable Jacket Formulation
(discontinued **) Elvax® 40L-08 high temperature ignition cable jacket.Information provided by DuPont. |
|||
Tensile Strength at Break | 9.40 MPa | 1360 psi | ASTM D638 |
ELASTO UK Dryflex® 650600 TPE, Improved Compression Set and High Temperature Resistance, 60A Hardness The VTC TPE Group have developed endless formulations to fulfill different properties and application requirements to optimize the finished component. This grade is designed with improved compressi.. |