Polymer Property : Tensile Strength at Break = 13.4 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	13.4 MPa	1940 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable 1604-xx27FRD Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength at Break	13.4 MPa @Temperature 23.0 °C	1940 psi @Temperature 73.4 °F	Die C2 hr; ASTM D412
PolyOne OnFlex™ HFFR 315-01 Thermoplastic Elastomer (TPE) OnFlex™ HFFR 315-01 a is non-halogen flame retardant material designed for flexible power cord insulation, cable jackets, and ribbon cables. New Product. Commercial specifications have not been est..
Tensile Strength at Break	13.4 MPa	1940 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ HC 2165 Polyvinyl Chloride, Flexible (PVC, Flexible) Geon HC 2165 is a 65 Shore A non-phthalate flexible vinyl compound made from FDA sanctioned ingredients. HC 2165 can be used for extrusion and injection molding healthcare applications.NOTE: All ing..
Tensile Strength at Break	13.4 MPa	1940 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ HC 2165G Polyvinyl Chloride, Flexible (PVC, Flexible) Geon HC 2165G is a 65 Shore A non-phthalate, gamma-stable flexible vinyl compound made from FDA sanctioned ingredients. HC 2165G can be used for extrusion and injection molding healthcare applicatio..
Tensile Strength at Break	13.4 MPa	1940 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible 90451 Polyvinyl Chloride, Flexible (PVC, Flexible) Automotive OEM approval(s).Information provided by PolyOne
Tensile Strength at Break	13.4 MPa	1940 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible MD403KB Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne
Tensile Strength at Break	13.4 MPa	1950 psi	ASTM D1414
Greene Tweed CHEMRAZÂ® 520 Perfluoroelastomer ChemrazÂ® 520 is recommended for a wide variety of semiconductor equipment dry processing applications where seal reliability with minimal contaminations is required. Additionally, Chemraz 520 of..
Tensile Strength at Break	13.4 MPa	1950 psi
Shin-Etsu Silicones FE-361TU Fluorosilicone Elastomer ShinEtsu FE361 TU is one of a series of high tensile, high tear translucent fluorosilicone compounds. It is designed to process well in molding applications. It can be blended with other members of ..
Tensile Strength at Break	13.4 MPa	1950 psi	ASTM D638
Teknor Apex APEXÂ® 3701-70NT Polyvinyl Chloride, Flexible Features: Non-DEHP Plasticizer; Ethylene Oxide Sterilizable; High Heat Resistance Uses: Medical/Healthcare Applications Processing Method: Extrusion Forms: PelletsInformation Provided by Teknor Apex..
Tensile Strength at Break	13.4 MPa	1950 psi	ASTM D412
Teknor Apex MonpreneÂ® MP-2264B Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo..
Tensile Strength at Break	13.4 MPa	1950 psi	Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C
3M Dyneon™ FT 2430 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FT 2430 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul..
Tensile Strength at Break	13.4 MPa	1950 psi	AVG; ASTM D412 Method A
Seals Eastern 5717 Fluorocarbon-Elastomer FKM. General service.Information provided by Seals Eastern, Inc.