Polymer Property : Tensile Strength at Break = 12.7 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	12.7 MPa	1840 psi	ISO R 527
Stir SpA AF SG 76 CZ OIL (PVC) Application: Extrusion flame resistant oil-proof sheath, ecologicalInformation provided by STIR SpA
Tensile Strength at Break	12.7 MPa	1840 psi	500 mm/min (20 in./min); ASTM-D638 Type IV Specimen
Westlake EMAC® SP2404 18.5% EMA Copolymer Westlake EMACï¿½ SP2404 is a 18.5% EMA copolymer designed for blown film, tie-layer, coextrusions, and blending where flexibility and strength are important. SP2404 provides excellent elasticity ..
Tensile Strength at Break	12.7 MPa	1840 psi	ASTM D638
Unitika elitel UE3700 Polyester, Pellet Hot melt adhesives, Adhesives for fibers, Adhesives for interlining clothsUNITIKA l resins are thermoplastic saturated copolymeric polyester resins. l resins are expanding their applications from p..
Tensile Strength at Break	12.7 MPa	1840 psi	ASTM D638
Unitika elitel UE3800 Polyester, Pellet Hot melt adhesives, Adhesives for polyvinylchlorideUNITIKA l resins are thermoplastic saturated copolymeric polyester resins. l resins are expanding their applications from products such as adhesiv..
Tensile Strength at Break	12.7 MPa	1840 psi
Daikin DAI-EL G-704 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Information provided by Daikin Industries.