Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Ball Indentation Hardness | 90.0 - 270 MPa | 13100 - 39200 psi | Average value: 191 MPa Grade Count:5 |
Overview of materials for Nylon 6, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of a.. |
|||
Ball Indentation Hardness | 80.0 - 270 MPa | 11600 - 39200 psi | Average value: 180 MPa Grade Count:22 |
Overview of materials for Nylon 66/6, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are incl.. |
|||
Ball Indentation Hardness | 160 - 270 MPa | 23200 - 39200 psi | Average value: 223 MPa Grade Count:3 |
Overview of materials for Nylon 66, 20% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Carbon Fiber Filled". Specific grades with carbon fiber content between 15% and 24% are in.. |
|||
Ball Indentation Hardness | 200 - 270 MPa @Time 30.0 sec |
29000 - 39200 psi @Time 0.00833 hour |
DIN 53 456 |
Hippe PA 66 GF 30 Nylon 66 30% Glass fiber Reinforced These polyamide components being reinforced with glass fiber up to 30% are not only highly wear-resistant, but also show high mechanical strength, stiffness and dimensional stability. They can also.. |