Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Ball Indentation Hardness | 70.0 - 150 MPa | 10200 - 21800 psi | ISO.2039-2 |
Polimersan Plastics POLIPA® (PA 6) Polyamide POLIPA® PA6 (POLYAMIDE) is produced by poly condensation of e-aminoacid and by the help of d-carbon acid and d-amine poly condensation. Its characteristics depend upon the numbers of the main struc.. |
|||
Ball Indentation Hardness | 70.0 - 150 MPa | 10200 - 21800 psi | ISO.2039-2 |
Polimersan Plastics POLIPA® (PA 6) Polyamide POLIPA® PA6 (POLYAMIDE) is produced by poly condensation of e-aminoacid and by the help of d-carbon acid and d-amine poly condensation. Its characteristics depend upon the numbers of the main struc.. |
|||
Ball Indentation Hardness | 66.0 - 150 MPa | 9570 - 21800 psi | Average value: 138 MPa Grade Count:13 |
Overview of materials for Polystyrene, Molded, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene". Each property range of values reported is minimum and maximum values of appropriate MatWeb.. |
|||
Ball Indentation Hardness | 81.0 - 150 MPa | 11700 - 21800 psi | Average value: 140 MPa Grade Count:16 |
Overview of materials for Polystyrene, Heat Resistant Grade This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Heat Resistant Grade". Each property range of values reported is minimum and maximum values.. |
|||
Ball Indentation Hardness | 110 - 150 MPa | 16000 - 21800 psi | Average value: 129 MPa Grade Count:9 |
Overview of materials for Nylon 66, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum .. |
|||
Ball Indentation Hardness | 110 - 150 MPa | 16000 - 21800 psi | ISO 2032 |
Adamas Adalon® 466 PTFE, Mineral/Organic Filler Information provided by Adamas, HPM |
|||
Ball Indentation Hardness | 70.0 - 150 MPa | 10200 - 21800 psi | Average value: 112 MPa Grade Count:3 |
Overview of materials for Nylon 6, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum v.. |
|||
Ball Indentation Hardness | 76.0 - 150 MPa | 11000 - 21800 psi | Average value: 125 MPa Grade Count:3 |
Overview of materials for Polystyrene, Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Extrusion Grade". Each property range of values reported is minimum and maximum values of a.. |
|||
Ball Indentation Hardness | 70.0 - 150 MPa | 10200 - 21800 psi | Average value: 109 MPa Grade Count:11 |
Overview of materials for Nylon 6, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Impact Grade". Each property range of values reported is minimum and maximum values of appropri.. |