Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Yield, MD | 20.0 MPa @Thickness 0.430 mm, Temperature 23.0 °C |
2900 psi @Thickness 0.0169 in, Temperature 73.4 °F |
ASTM D638 |
Mapal Plastics Maplon CFA-HK Polypropylene Sheet Applications: For use with electrical insulation products. For use when flame retardant and static dissipative properties are required. |
|||
Film Tensile Strength at Yield, MD | 20.0 MPa @Thickness 0.250 mm, Temperature 23.0 °C |
2900 psi @Thickness 0.00984 in, Temperature 73.4 °F |
ASTM D638 |
Mapal Plastics Maplon CFA-HK Polypropylene Sheet Applications: For use with electrical insulation products. For use when flame retardant and static dissipative properties are required. |
|||
Film Tensile Strength at Yield, MD | 20.0 MPa @Thickness 0.0200 mm |
2900 psi @Thickness 0.000787 in |
ISO 527-3 |
Total MDPE HF 513 Medium Density Polyethylene, Blown Film MDPE HF 513 is a medium density polyethylene produced by slurry loop low pressure process with hexene as co-monomer.MDPE HF 513 is a semi-high molecular weight polyethylene giving excellent mechanic.. |
|||
Film Tensile Strength at Yield, MD | 20.0 MPa @Thickness 0.0400 mm |
2900 psi @Thickness 0.00157 in |
ISO 527-3 |
Total MDPE HT 514 Medium Density Polyethylene, Blown Film MDPE HT 514 is a medium density polyethylene produced by slurry loop low pressure process with hexene as co-monomer.MDPE HT 514 is a semi-high molecular weight polyethylene giving excellent mechanic.. |