Polymer Property : Compressive Modulus = 3.00 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Modulus	3.00 GPa	435 ksi	Type B, 5mm/min; ISO 604:2002
Nylacast Nylube GF Cast Nylon 6, Lubricated (Blended Solid and Liquid Lubricant), Glass Filled For applications requiring higher compressive strength the NYLUBE GF masterbatch incorporates hollow glass ovule, designed to float and evenly distribute through the polymerising polymer. The glass ..
Compressive Modulus	3.00 GPa	435 ksi	ISO 604
Polikim KESTAMID® GRF Polyamide 6, Graphite Filled Graphite and special lubricants are evenly dispersed in its entirety in this type of Polikim's cast polyamide. The material is dark grey colored. Kestamid®-GRF has a high degree of crystallinity an..
Compressive Modulus	3.00 GPa	435 ksi
MarkeTech Carbon Aerogel Data provided by the supplier, MarkeTech International.Availability: Paper Sheets: 85 x 250 mm; Random Pieces 0.5-20 mm; Granules and Powder.Resorcinol Formaldehyde and Silica Aerogels are also list..
Compressive Modulus	3.00 GPa	435 ksi	Sample Type A, 1 mm/min; ISO 604:2002
Global EPP PA 6C MOLY Cast Polyamide 6 + MoS2 Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of ..
Compressive Modulus	3.00 GPa	435 ksi	Stabilized, typ
Hexcel® HexWeb® CR III 1/8-5056-.002 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR..
Compressive Modulus	3.00 GPa	435 ksi	Stabilized, typ
Hexcel® HexWeb® CR-PAA™ 1/8-5056-0.002 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa..