Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Yield Strength | 140 - 186 MPa | 20300 - 27000 psi | Average value: 178 MPa Grade Count:10 |
Overview of materials for Diallyl Phthalate (DAP) Molding Compound, Long Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Diallyl Phthalate (DAP) Molding Compound, Long Glass Fiber Filled". Each property range of values report.. |
|||
Compressive Yield Strength | 140 MPa | 20300 psi | ISO 14126 |
Menzolit Menzolit® SMC 1400 Unsaturated Polyester UP SMC 1400 is a special SMC being used in the environment of a combustion engine. The glass level has been selected to combine good mouldability with good stiffness and strength properties. The produc.. |
|||
Compressive Yield Strength | 140 MPa | 20300 psi | |
Haveg 61NA Furfuryl Alcohol-Formaldehyde Resin A proprietary thermoset plastic consisting of a furfuryl alcohol-formaldehyde resin and non-asbestos silicate fillers. |
|||
Compressive Yield Strength | 140 MPa @Temperature 100 °C |
20300 psi @Temperature 212 °F |
90º, Wet; DIN65380 |
Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, TVR380/26% Fiber Information provided by HexCel |
|||
Compressive Yield Strength | 140 - 222 MPa | 20300 - 32200 psi | Average value: 166 MPa Grade Count:11 |
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Compressive Yield Strength | 140 MPa | 20300 psi | Compression After Impact @ 6.6 J/mm, Results normalized to 60% fibre volume for Carbon, 50% fibre volume for Kevlar; pr EN 6038 |
Hexcel® HexPly® 920KX-285-52% 125°C Curing Epoxy Matrix Kevlar, 4H satin, 171 g/m2Information provided by HexCel |