Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Yield Strength | 124 - 198 MPa | 18000 - 28700 psi | Average value: 175 MPa Grade Count:7 |
Overview of materials for Polyetherimide (PEI), 20% Glass Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 20% Glass Fiber". Specific grades with glass content between 15% and 24% are included. E.. |
|||
Compressive Yield Strength | 124 - 221 MPa | 18000 - 32000 psi | Average value: 182 MPa Grade Count:8 |
Overview of materials for Polyetherimide (PEI), 30% Glass Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 30% Glass Fiber". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Compressive Yield Strength | 124 MPa | 18000 psi | ASTM D695 |
Spartech Polycast Cell Cast Acrylic Description: Cell Cast AcrylicInformation provided by Spartech. |
|||
Compressive Yield Strength | 124 MPa | 18000 psi | ASTM D695 |
Spartech Polycast Poly 76 (Mil-P-8184) Cell Cast Acrylic Description: Cell Cast AcrylicInformation provided by Spartech. |
|||
Compressive Yield Strength | 124 MPa | 18000 psi | ASTM D695 |
Spartech Polycast Poly 84 (Mil-P-8184) Cell Cast Acrylic Description: Cell Cast AcrylicInformation provided by Spartech. |
|||
Compressive Yield Strength | 124 MPa | 18000 psi | ASTM D695 |
Spartech Polycast Poly II (Mil-P-5425) Cell Cast Acrylic Description: Cell Cast AcrylicInformation provided by Spartech. |
|||
Compressive Yield Strength | 124 MPa | 18000 psi | ASTM D695 |
Spartech Polycast UF3 Cell Cast Acrylic Description: Cell Cast AcrylicInformation provided by Spartech. |
|||
Compressive Yield Strength | 124 MPa | 18000 psi | ASTM D695 |
Spartech Polycast UF4 Cell Cast Acrylic Description: Cell Cast AcrylicInformation provided by Spartech. |
|||
Compressive Yield Strength | 124 MPa | 18000 psi | ASTM D695 |
Spartech Polycast UF96 Cell Cast Acrylic Description: Cell Cast AcrylicInformation provided by Spartech. |
|||
Compressive Yield Strength | 124 MPa | 18000 psi | ASTM D695 |
Spartech Polycast UVT (Ultra-Violet Transmitting) Cell Cast Acrylic Description: Cell Cast AcrylicInformation provided by Spartech. |
|||
Compressive Yield Strength | 124 MPa | 18000 psi | 10% Strain; EN ISO 604 |
Ensinger TECASINT™ 2031 Polyimide, 40% Graphite Filled (PI) TECASINT™ 2000 series of polyimide stock shapes provide a superior combination of high temperature and bearing and wear, properties that make it an ideal choice for the most demanding applications... |
|||
Compressive Yield Strength | 124.1 MPa | 18000 psi | |
Abatron AboCast/AboCure 8109-11 All-purpose, structural dielectric resin. Better thermal and chemical properties than 8109-8, but requires heat cure. Melts at 70-80°C and remains liquid (supercooled) for many hours at RT.Process.. |
|||
Compressive Yield Strength | 124.1 MPa | 18000 psi | |
Abatron AboCast/AboCure 8109-8 All-purpose, structural dielectric resin. High thermal and chemical resistance and RT cure.Processing: 100/12 ratio; Potlife: 45 min/20°C (68°F), 20 min/40°C (105°F), 10 min /60°C (140°F); mi.. |
|||
Compressive Yield Strength | 124 MPa | 18000 psi | ASTM D695 |
Adell AT-13 Nylon 66, 15% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc. |
|||
Compressive Yield Strength | 124 MPa | 18000 psi | ASTM D695 |
Adell BJ-14 Nylon 6, 20% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
Compressive Yield Strength | 124 MPa | 18000 psi | ASTM D695 |
Adell BJ-34 Nylon 6, 20% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
Compressive Yield Strength | 124 MPa | 18000 psi | ASTM D695 |
Adell HR-36 30% Glass Reinforced Heat Stabilized PBT |
|||
Compressive Yield Strength | 124 - 145 MPa | 18000 - 21000 psi | Average value: 140 MPa Grade Count:5 |
Overview of materials for Polyethersulfone (PES), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% .. |
|||
Compressive Yield Strength | 124.1 MPa | 18000 psi | |
Abatron AboCast/AboCure 8109-7 Processing: 100/80 pbw; Potlife: 6-7 days/20°C (68°F), 12-24 h/40°C (105°F), 0.75-7 h /60°C (140°F); mix at 50-80°C (120-175°F); cures in: 1 h/100°C (212°F) + 4 h/150°C (300°F) postcure... |
|||
Compressive Yield Strength | 124 MPa | 18000 psi | ASTM D695 |
Adell AT-33 Nylon 66, 15% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc. |