Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Yield Strength | 110 - 138 MPa | 16000 - 20000 psi | Average value: 120 MPa Grade Count:7 |
Overview of materials for Polycarbonate, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 30% Glass Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Compressive Yield Strength | 110 - 380 MPa | 16000 - 55100 psi | Average value: 237 MPa Grade Count:63 |
Overview of materials for Phenolic, Novolac, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Glass Filled". Each property range of values reported is minimum and maximum values o.. |
|||
Compressive Yield Strength | 110 MPa | 16000 psi | 10% Deflection; ASTM D-695 |
Aardvark Polymers AARTEL® 820UV Acetal Copolymer Rotational Molding Resin Aartel 820UV is a natural acetal copolymer with added UV stabilizers.Aartel 820UV is a low viscosity resin with excellent flow characteristics.Aartel 820UV is available in natural white and may be p.. |
|||
Compressive Yield Strength | 110 MPa | 16000 psi | |
Cytec Thornel® Graphite Cloth Laminate with Mil R-9299 Resin Data provided by the manufacturer, Amoco Performance Products, Inc.Carbon and graphite cloths, consisting entirely of flexible filaments, are produced by pyrolysis of rayon cloth at high temperature.. |
|||
Compressive Yield Strength | 110 MPa @Strain 10.0 %, Temperature 23.0 °C |
16000 psi @Strain 10.0 %, Temperature 73.4 °F |
EN ISO 604 |
Ensinger TECASINT™ 2032 Polyimide, Black, 40% Graphite (PI) TECASINT™ 2000 series of polyimide stock shapes provide a superior combination of high temperature and bearing and wear, properties that make it an ideal choice for the most demanding applications... |
|||
Compressive Yield Strength | 110 MPa | 16000 psi | ASTM D695 |
Adell AJ-13 Nylon 66, 15% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
Compressive Yield Strength | 110 MPa | 16000 psi | ASTM D695 |
Adell AJ-33 Nylon 66, 15% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
Compressive Yield Strength | 110 MPa | 16000 psi | ASTM D695 |
Techmer ES Plaslube® J-50/30/TF/15 Polycarbonate, 30% Glass Reinforced, PTFE Lubricated 30% Glass Reinforced, PTFE Lubricated |
|||
Compressive Yield Strength | 110 MPa | 16000 psi | Average value: 110 MPa Grade Count:3 |
Overview of materials for Polyethersulfone (PES), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% a.. |
|||
Compressive Yield Strength | 110 - 124 MPa | 16000 - 18000 psi | Average value: 114 MPa Grade Count:4 |
Overview of materials for Acrylic, Cast This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Cast". Each property range of values reported is minimum and maximum values of appropriate MatW.. |