Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 150 GPa @Temperature 927 °C |
21800 ksi @Temperature 1700 °F |
|
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Modulus of Elasticity | 150 GPa @Temperature 927 °C |
21800 ksi @Temperature 1700 °F |
|
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Modulus of Elasticity | 150 GPa @Temperature 927 °C |
21800 ksi @Temperature 1700 °F |
|
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Modulus of Elasticity | 150 GPa @Temperature 927 °C |
21800 ksi @Temperature 1700 °F |
|
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1121°C, air cooled, aged 16 hours at 899°C Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Modulus of Elasticity | 150 GPa @Temperature 500 °C |
21800 ksi @Temperature 932 °F |
Typical annealed sample; short time elevated temp. |
American Utility Metals Cromgard® Stainless Steel Cromgard is a low cost stainless steel, which is able to provide benefits of good weldability and formability, making it capable of fabrication by conventional techniques. It provides the benefits o.. |
|||
Modulus of Elasticity | 150 GPa @Temperature 927 °C |
21800 ksi @Temperature 1700 °F |
|
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include .. |