Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Adhesive Bond Strength | 2.07 MPa | 300 psi | Aluminum to aluminum |
Momentive Performance Materials TSE322 Heat-Curing Silicone Adhesive, Light Blue RTV6424, RTV6445, and TSE322 silicone adhesives are one-component heat curable silicone adhesive sealants which will bond to many substrates without a primer and which will creep rapidly at elevated.. |
|||
Adhesive Bond Strength | 2.07 MPa | 300 psi | Aluminum to aluminum |
Momentive Performance Materials TSE322B Heat-Curing Silicone Adhesive, Black RTV6424, RTV6445, and TSE322 silicone adhesives are one-component heat curable silicone adhesive sealants which will bond to many substrates without a primer and which will creep rapidly at elevated.. |
|||
Adhesive Bond Strength | 2.07 MPa | 300 psi | |
Trelleborg Emerson & Cuming Eccobond® 59C One-Component Silver Filled Electrically Conductive Silicone Adhesive Emerson & Cuming 59C Eccobond® One-Component Silver Filled Electrically Conductive Silicone AdhesiveOne component, solvent containing, silver filled, electrically conductive, silicone pressure sens.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (no primer) Concrete Failure; ASTM D4541 Elcometer |
ACC EP AEP EPI Engineered Polymers EP AEP is a new generation of Internetwork Polymers of polyurea and Epoxy, “Powered by Reactamine® Technology”. EP AEP was developed for a colorfast floor for both residential and industrial appl.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (primer), Concrete Failure; ASTM D4541 Elcometer |
ACC EP AEP EPI Engineered Polymers EP AEP is a new generation of Internetwork Polymers of polyurea and Epoxy, “Powered by Reactamine® Technology”. EP AEP was developed for a colorfast floor for both residential and industrial appl.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (epoxy), Concrete Failure; ASTM D4541 Elcometer |
ACC EP AEP EPI Engineered Polymers EP AEP is a new generation of Internetwork Polymers of polyurea and Epoxy, “Powered by Reactamine® Technology”. EP AEP was developed for a colorfast floor for both residential and industrial appl.. |
|||
Adhesive Bond Strength | 2.07 MPa | 300 psi | Concrete (epoxy), Concrete Failure; ASTM D4541 Elcometer |
ACC EP EF EPI Engineered Polymers Extra Flex Polyurea EP EF, Extra Flex Polyurea, “Powered by Reactamine® Technology, is a two component 100% solid Polyurea, with superior performance in industrial applications. EP EF displays extremely fast cure tim.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (no primer), Concrete Failure; ASTM D4541 Elcometer |
ACC EP QSZ EPI Engineered Polymers Quick Set Epoxy with Zinc EP QSZ Quick Set Epoxy with Zinc, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC’s (Volatile Organic Compound), self-leveling modified epoxy. This versatile new gene.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (no primer), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RAP 45 EPI Engineered Polymers Aliphatic Polyurea EP RAP 45 Aliphatic Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC is, aliphatic polyurea (silicone optional) coating, that was developed for UV stable (col.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (primer), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RAP-1567 EPI Engineered Polymers Aliphatic Polyurea RAP-1567 HX is a two component 100% solids, no VOC’s, aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This new generat.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (epoxy), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RAP-1567 EPI Engineered Polymers Aliphatic Polyurea RAP-1567 HX is a two component 100% solids, no VOC’s, aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This new generat.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (no primer), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RAP-1567 HX EPI Engineered Polymers Aliphatic Polyurea RAP-1567 is a two component 100% solids, no VOC’s, aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This new generation.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (primer), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RAP-1567 SP-HX EPI Engineered Polymers Silicone Aliphatic Polyurea RAP-1567 SP is a two component 100% solids, no VOC’s, silicone aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This ne.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (epoxy), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RAP-1567 SP-HX EPI Engineered Polymers Silicone Aliphatic Polyurea RAP-1567 SP is a two component 100% solids, no VOC’s, silicone aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This ne.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (no primer), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RAP-1567 SP-HX EPI Engineered Polymers Silicone Aliphatic Polyurea RAP-1567 SP is a two component 100% solids, no VOC’s, silicone aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This ne.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (primer), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RAP-1567 SP-HX EPI Engineered Polymers Silicone Aliphatic Polyurea RAP-1567 SP-HX is a two component 100% solids, no VOC’s, silicone aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (epoxy), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RAP-1567 SP-HX EPI Engineered Polymers Silicone Aliphatic Polyurea RAP-1567 SP-HX is a two component 100% solids, no VOC’s, silicone aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (no primer), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RAP-1567 SP-HX EPI Engineered Polymers Silicone Aliphatic Polyurea RAP-1567 SP-HX is a two component 100% solids, no VOC’s, silicone aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This.. |
|||
Adhesive Bond Strength | 2.07 MPa | 300 psi | Concrete (epoxy), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RASP EPI Engineered Polymers Aliphatic Silicone Polymer EP RASP Aliphatic Silicone Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solid Polyurea that has excellent UV stability (colorfast) with superior performance in industria.. |
|||
Adhesive Bond Strength | 2.07 MPa | 300 psi | Concrete (epoxy), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RSP-AL EPI Engineered Polymers Aromatic Silicone Polyurea EP RSP-AL, Aromatic Silicone Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solid Polyurea. This increases UV resistance without sacrificing physical properties. EP RSP-AL.. |
|||
Adhesive Bond Strength | 2.07 MPa | 300 psi | Concrete (epoxy), Concrete Failure; ASTM D4541 Elcometer |
ACC SMP™ EP EF SP EPI Engineered Polymers Extra Flex with Silicone EP EF SP, “Powered by Reactamine® Technology”, is a two component 100% solid Silicone Polyurea with superior performance in industrial applications. EP EF SP displays extremely fast cure times wi.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (primer), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RAP 60 EPI Engineered Polymers Aliphatic Polyurea EP RAP 60 Aliphatic Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC, coating (silicone optional) developed for UV stable (colorfast) polyurea flooring applic.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (no primer), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RAP 60 EPI Engineered Polymers Aliphatic Polyurea EP RAP 60 Aliphatic Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC, coating (silicone optional) developed for UV stable (colorfast) polyurea flooring applic.. |
|||
Adhesive Bond Strength | 2.07 MPa | 300 psi | Concrete (epoxy), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RSP EPI Engineered Polymers Silicone Polyurea EP RSP Silicone Polyurea, “Powered by Reactamine®Technology”, is a two component 100% solid Polyurea with superior performance in industrial applications. EP RSP displays extremely fast cure time.. |
|||
Adhesive Bond Strength | 2.07 MPa | 300 psi | Concrete (epoxy), Concrete Failure; ASTM D4541 Elcometer |
ACC SMP™ EP 1009 EPI Engineered Polymers Silicone Modified Polymer EP 1009, “Powered by Reactamine®Technology”, is a two component 100% solid Silicone Modified Polyurea with superior performance in industrial applications. EP 1009 displays extremely fast cure ti.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (no primer), Concrete Failure; ASTM D4541 Elcometer |
ACC EP QS EPI Engineered Polymers Quick Set Epoxy EP QS Quick Set Epoxy, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC, self-leveling modified epoxy. This versatile new generation epoxy displays low blush, fast cure.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (epoxy), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RAP 45 14 EPI Engineered Polymers Aliphatic Polyurea EP RAP 45 14 Aliphatic Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC’s, aliphatic polyurea coating that was developed for UV stable (colorfast) polyurea f.. |
|||
Adhesive Bond Strength | >= 2.07 MPa | >= 300 psi | Concrete (no primer), Concrete Failure; ASTM D4541 Elcometer |
ACC EP RAP 45 14 EPI Engineered Polymers Aliphatic Polyurea EP RAP 45 14 Aliphatic Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC’s, aliphatic polyurea coating that was developed for UV stable (colorfast) polyurea f.. |
|||
Adhesive Bond Strength | 2.07 MPa | 300 psi | Concrete (epoxy), Concrete Failure; ASTM D4541 Elcometer |
ACC ReactAmine® EP 350 EPI Engineered Polymers Polyurea ReactAmine® EP-350 is a two component 100% solid Polyurea with superior performance in industrial applications. EP-350 displays extremely fast cure times with excellent adhesions to different subst.. |