Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 10.0 - 16.0 GPa | 1450 - 2320 ksi | Injection; ISO 527 |
Raschig Group 5553 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Modulus of Elasticity | 14.0 - 16.0 GPa | 2030 - 2320 ksi | Injection and Compression; ISO 527 |
Raschig Group EPOXIDUR® 3580 EP Epoxy Glass-fiber reinforced and mineral filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties even with thin wall thicknesses and high temperatures. This prod.. |
|||
Modulus of Elasticity | 1.17 - 16.0 GPa | 170 - 2320 ksi | Average value: 4.07 GPa Grade Count:46 |
Overview of materials for Polyetheretherketone, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, PTFE Filled". Each property range of values reported is minimum and maximum values.. |
|||
Modulus of Elasticity | 7.20 - 16.0 GPa @Temperature 60.0 - 150 °C |
1040 - 2320 ksi @Temperature 140 - 302 °F |
Average value: 11.7 GPa Grade Count:2 |
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Modulus of Elasticity | 1.90 - 16.0 GPa | 276 - 2320 ksi | Average value: 4.99 GPa Grade Count:57 |
Overview of materials for Nylon 6, 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% are included. .. |