Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	196 GPa	28400 ksi	RT
Outokumpu 4833 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and ..
Modulus of Elasticity	196 GPa @Temperature 300 Â°C	28400 ksi @Temperature 572 Â°F
Haynes 230Â® alloy, 20% cold reduction, 1177Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Modulus of Elasticity	196 GPa @Temperature 300 Â°C	28400 ksi @Temperature 572 Â°F
Haynes 230Â® alloy, 30% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Modulus of Elasticity	196 GPa @Temperature 204 Â°C	28400 ksi @Temperature 399 Â°F	plate heat treated to 1177Â°C and rapid quenched
Haynes HastelloyÂ® G-30Â® alloy, all-weld metal, GTAW weld 3.2 mm diameter filler wire HASTELLOYÂ® G-30Â® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid..
Modulus of Elasticity	196 GPa	28400 ksi
Industeel SIRIUS 800 Heat Resistant Alloy Description: The SIRIUSÂ® 800, H and H+ grades are three variants of a high chromium and nickel austenitic alloy which combines good corrosion and creep resistance. SIRIUSÂ® 800 is employed at t..
Modulus of Elasticity	196 GPa @Temperature 204 Â°C	28400 ksi @Temperature 399 Â°F	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, 10% cold worked sheet HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	196 GPa @Temperature 204 Â°C	28400 ksi @Temperature 399 Â°F	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, 20% cold worked sheet, aged 100 hours at 500Â°C HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	196 GPa @Temperature 204 Â°C	28400 ksi @Temperature 399 Â°F	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, GTAW, aged 4000 hours at 450Â°C (800Â°F), notched HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	196 GPa @Temperature 204 Â°C	28400 ksi @Temperature 399 Â°F	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, GTAW, aged 4000 hours at 450Â°C (800Â°F), unnotched HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	196 GPa @Temperature 204 Â°C	28400 ksi @Temperature 399 Â°F	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, GTAW, as welded, notched HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	196 GPa @Temperature 204 Â°C	28400 ksi @Temperature 399 Â°F	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, SMAW weld, C-22 base metal, C-22 weld metal HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	196 GPa @Temperature 204 Â°C	28400 ksi @Temperature 399 Â°F	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, transverse, GMAW short arc weldment, plate HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	196 GPa @Temperature 204 Â°C	28400 ksi @Temperature 399 Â°F	heat-treated at 1121Â°C (2050Â°F), rapid quenched, plate
Haynes HastelloyÂ® C-22Â® alloy, transverse, GTAW weldment, sheet - plate HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Modulus of Elasticity	196 GPa @Temperature 204 Â°C	28400 ksi @Temperature 399 Â°F	plate heat treated to 1177Â°C and rapid quenched
Haynes HastelloyÂ® G-30Â® alloy, 3.2 mm thick sheet, GTAW weld HASTELLOYÂ® G-30Â® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid..
Modulus of Elasticity	196 GPa @Temperature 204 Â°C	28400 ksi @Temperature 399 Â°F	plate heat treated to 1177Â°C and rapid quenched
Haynes HastelloyÂ® G-30Â® alloy, 50% cold rolled HASTELLOYÂ® G-30Â® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid..
Modulus of Elasticity	196 GPa @Temperature 204 Â°C	28400 ksi @Temperature 399 Â°F	plate heat treated to 1177Â°C and rapid quenched
Haynes HastelloyÂ® G-30Â® alloy, 50% cold rolled and 5000 hours at 500Â°C, air cooled HASTELLOYÂ® G-30Â® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid..
Modulus of Elasticity	196 GPa @Temperature 204 Â°C	28400 ksi @Temperature 399 Â°F	plate heat treated to 1177Â°C and rapid quenched
Haynes HastelloyÂ® G-30Â® alloy, plate and bar HASTELLOYÂ® G-30Â® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid..
Modulus of Elasticity	196 GPa	28400 ksi	RT
Outokumpu 4948 High Temperature Austenitic Stainless Steel Creep-resistant variant of 1.4301, with a standardized minimum carbon content for service at temperatures of up to 800°C in dry air.Applications: Heat and creep resistance. For use over 550°C for..
Modulus of Elasticity	196 GPa	28400 ksi
Industeel SIRIUS 800 H Heat Resistant Alloy Description: The SIRIUS® 800, H and H+ grades are three variants of a high chromium and nickel austenitic alloy which combines good corrosion and creep resistance. SIRIUS® 800 is employed at tempe..
Modulus of Elasticity	196 GPa @Temperature 300 °C	28400 ksi @Temperature 572 °F
Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..
Modulus of Elasticity	196 GPa @Temperature 300 °C	28400 ksi @Temperature 572 °F
Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..
Modulus of Elasticity	196 GPa @Temperature 300 °C	28400 ksi @Temperature 572 °F
Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..
Modulus of Elasticity	196 GPa @Temperature 204 °C	28400 ksi @Temperature 399 °F	heat-treated at 1121°C (2050°F), rapid quenched, plate
Haynes Hastelloy® C-22® alloy, all-weld metal, SMAW HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..
Modulus of Elasticity	196 GPa @Temperature 204 °C	28400 ksi @Temperature 399 °F	heat-treated at 1121°C (2050°F), rapid quenched, plate
Haynes Hastelloy® C-22® alloy, GTAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..
Modulus of Elasticity	196 GPa @Temperature 204 °C	28400 ksi @Temperature 399 °F	plate heat treated to 1177°C and rapid quenched
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW short arc weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin..
Modulus of Elasticity	196 GPa @Temperature 204 °C	28400 ksi @Temperature 399 °F	plate heat treated to 1177°C and rapid quenched
Haynes Hastelloy® G-30® alloy, 19.1 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin..
Modulus of Elasticity	196 GPa @Temperature 300 °C	28400 ksi @Temperature 572 °F
Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..
Modulus of Elasticity	196 GPa @Temperature 204 °C	28400 ksi @Temperature 399 °F	heat-treated at 1121°C (2050°F), rapid quenched, plate
Haynes Hastelloy® C-22® alloy, 0% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..
Modulus of Elasticity	196 GPa @Temperature 204 °C	28400 ksi @Temperature 399 °F	heat-treated at 1121°C (2050°F), rapid quenched, plate
Haynes Hastelloy® C-22® alloy, 60% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..
Modulus of Elasticity	196 GPa @Temperature 204 °C	28400 ksi @Temperature 399 °F	heat-treated at 1121°C (2050°F), rapid quenched, plate
Haynes Hastelloy® C-22® alloy, SMAW weld, 904L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..