Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 173 GPa @Temperature 595 °C |
25100 ksi @Temperature 1100 °F |
|
Haynes HR-160® alloy plate, aged 1000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 173 GPa @Temperature 595 °C |
25100 ksi @Temperature 1100 °F |
|
Haynes HR-160® alloy plate, aged 4000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 173 GPa @Temperature 595 °C |
25100 ksi @Temperature 1100 °F |
|
Haynes HR-160® alloy, annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 173 GPa @Temperature 595 °C |
25100 ksi @Temperature 1100 °F |
|
Haynes HR-160® alloy, hot rolled and solution annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 173 GPa @Temperature 595 °C |
25100 ksi @Temperature 1100 °F |
|
Haynes HR-160® alloy, plate, aged 1000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 173 GPa @Temperature 595 °C |
25100 ksi @Temperature 1100 °F |
|
Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 173 GPa @Temperature 595 °C |
25100 ksi @Temperature 1100 °F |
|
Haynes HR-160® alloy, plate, aged 4000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 173 GPa @Temperature 595 °C |
25100 ksi @Temperature 1100 °F |
|
Haynes HR-160® alloy, plate, aged 4000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 173 GPa @Temperature 595 °C |
25100 ksi @Temperature 1100 °F |
|
Haynes HR-160® alloy, plate, aged 8000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 173 GPa @Temperature 595 °C |
25100 ksi @Temperature 1100 °F |
|
Haynes HR-160® alloy, plate, aged 8000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 173 GPa @Temperature 595 °C |
25100 ksi @Temperature 1100 °F |
|
Haynes HR-160® alloy, solution annealed sheet Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 173 GPa @Temperature 500 °C |
25100 ksi @Temperature 932 °F |
|
Haynes 718 alloy, cold rolled, solution-treated and aged sheet Cb and Ta content combined weight percentage of 5. Excellent high-temperature strength up to 650°C, good ductility, formability, and weldability. Very good welding characteristics. Applications i.. |
|||
Modulus of Elasticity | 173 GPa @Temperature 595 °C |
25100 ksi @Temperature 1100 °F |
|
Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 173 GPa | 25100 ksi | ASTM-C848 |
CoorsTek ZDY Yttria Fully Stabilized Zirconia Oxygen ionic conductor for high-stress and high-thermal-shock environments |
|||
Modulus of Elasticity | 173 GPa @Temperature 400 °C |
25100 ksi @Temperature 752 °F |
|
Assab Steels ASSAB XW-41 Cold Work Steel XW-41 is a high-carbon, high chromium tool steel alloyed with molybdenum and vanadium characterized by:High wear resistanceHigh compressive strength Good through-hardening propertiesHigh stability i.. |
|||
Modulus of Elasticity | 173 GPa @Temperature 400 °C |
25100 ksi @Temperature 752 °F |
|
Assab Steels ASSAB XW-42 Cold Work Steel XW-42 is a high-carbon, high chromium tool steel alloyed with molybdenum and vanadium characterized by:High wear resistanceHigh compressive strength High hardness after hardeningGood through-hardeni.. |
|||
Modulus of Elasticity | 173 GPa @Temperature 400 °C |
25100 ksi @Temperature 752 °F |
|
Assab Steels ASSAB XW-5 Cold Work Steel ASSAB XW-5 is a high-carbon, high chromium tool steel alloyed with tungsten, characterized by:High wear resistanceHigh compressive strengthHigh surface hardness after hardeningGood through-hardening.. |