- Polymer Property : Modulus of Elasticity = 21800 ksi
Polymer Property : Modulus of Elasticity = 21800 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 150 GPa @Temperature 1000 °C |
21800 ksi @Temperature 1830 °F |
|
| Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 150 GPa @Temperature 1000 °C |
21800 ksi @Temperature 1830 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 150 GPa @Temperature 1000 °C |
21800 ksi @Temperature 1830 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 150 GPa @Temperature 1000 °C |
21800 ksi @Temperature 1830 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 150 GPa @Temperature 1000 °C |
21800 ksi @Temperature 1830 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 150 GPa @Temperature 870 °C |
21800 ksi @Temperature 1600 °F |
|
| Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | ASTM C848 |
| CoorsTek Mullite, S2 Thermal Shock Delta Tc = 300°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | ASTM C848 |
| CoorsTek SC-BNL (SC-42) Loaded Reaction Bonded Silicon Carbide Thermal Shock Delta Tc = 137°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | |
| Alliance C-9B Strontium Ferrite Ceramic Magnetic Material |
|||
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Alliance N-35M Neodymium Iron Boron Magnetic Material |
|||
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Alliance N-35UH Neodymium Iron Boron Magnetic Material |
|||
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Alliance N-40H Neodymium Iron Boron Magnetic Material |
|||
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Alliance N-40SH Neodymium Iron Boron Magnetic Material |
|||
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Alliance N-42 Neodymium Iron Boron Magnetic Material |
|||
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Alliance N-44H Neodymium Iron Boron Magnetic Material |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | |
| Alliance S-26B Samarium Cobalt Magnetic Material |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | |
| Alliance S-28A Samarium Cobalt Magnetic Material |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | |
| Alliance S-28B Samarium Cobalt Magnetic Material |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | |
| Alliance S-30B Samarium Cobalt Magnetic Material |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | |
| Alliance C-8B Strontium Ferrite Ceramic Magnetic Material |
|||
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Alliance N-42H Neodymium Iron Boron Magnetic Material |
|||
| Modulus of Elasticity | 150 GPa @Temperature 1000 °C |
21800 ksi @Temperature 1830 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 150 GPa @Temperature 1000 °C |
21800 ksi @Temperature 1830 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 150 GPa @Temperature 1000 °C |
21800 ksi @Temperature 1830 °F |
|
| Haynes 230® alloy, 50% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||