Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 3.40 - 12.0 GPa | 493 - 1740 ksi | Average value: 6.02 GPa Grade Count:25 |
Overview of materials for Acetal Copolymer, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% ar.. |
|||
Modulus of Elasticity | 10.0 - 12.0 GPa | 1450 - 1740 ksi | Injection; ISO 527 |
Raschig Group RALUPOL® 8601 UP Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic moulding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical stren.. |
|||
Modulus of Elasticity | 10.0 - 12.0 GPa | 1450 - 1740 ksi | Injection; ISO 527 |
Raschig Group RALUPOL® 8602 UP Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic molding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical streng.. |
|||
Modulus of Elasticity | 2.90 - 12.0 GPa | 421 - 1740 ksi | Average value: 6.04 GPa Grade Count:155 |
Overview of materials for Nylon 66, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
Modulus of Elasticity | 3.45 - 12.0 GPa | 500 - 1740 ksi | Average value: 6.11 GPa Grade Count:18 |
Overview of materials for Polyethersulfone (PES), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% a.. |