- Polymer Property : Modulus of Elasticity = 148 GPa
Polymer Property : Modulus of Elasticity = 148 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 148 GPa | 21500 ksi | |
| Pacific Sintered Materials SS-316-RD 316L Stainless Steel Powdered Metal Non-magnetic, non-hardenable stainless steel for mechanical and instrumental components requiring corrosion resistance.Equivalent MPIF Specification: SS-316-40All information provided by Pacific Sin.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 30% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 50% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, all-weld metal GTAW Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, bar, after 0 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 316 °C |
21500 ksi @Temperature 600 °F |
|
| Latrobe Lescalloy® M50 VIM-VAR High Performance Bearing Steel LESCALLOY M50 VIM-VAR steel is a through-hardening grade with high hardness and high compressive strength at elevated temperatures. It is produced exclusively as a double vacuum melted produced usi.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||