Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 4.00 - 6.00 MPa | 580 - 870 psi | Cold Crushing Strength |
Gouda Vuurvast GI 26 Insulating Refractory Brick This data represents average values, obtained from samples that were cut from standard bricks.Information provided by Gouda Vuurvast. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin NEOFLON AP-210AS PFA Pellets NEOFLON PFA pellets have good melt flowability, and can be processed in the same manner as other thermoplastic resins.Applications: Anti-static grader for injection molding.Information provided by D.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin NEOFLON AP-230ASL PFA Pellets NEOFLON PFA pellets have good melt flowability, and can be processed in the same manner as other thermoplastic resins.Applications: Anti-static grader for extrusion molded parts. Piping, tube, etc... |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin NEOFLON NP-101 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding.Applications: High speed wire and cable coatings.Information pro.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin NEOFLON NP-120 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding.Applications: Heavy wall wire insulation, cable jacketing, tubes.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin NEOFLON NP-130 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion.Applications: Heavy wall wire insulation, cable jacketing, pipe, shrinka.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin NEOFLON NP-21 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding, injection molding.Applications: Suited to high speed extrusion .. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON F-104 PTFE Fine Powder Processing Methods: Paste extrusion, calendering.Applications: Unsintered tape, sealing tape, low specific gravity tape, tape for wrapping flat cables, tubes.Information provided by Daikin Industrie.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON F-201 PTFE Fine Powder Processing Methods: Paste extrusion.Applications: Spaghetti tubes, small diameter tubes, fine electric wire smaller than AGW16.Information provided by Daikin Industries. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON F-205 PTFE Fine Powder Processing Methods: Paste extrusion.Applications: Spaghetti tubes, small diameter tubes, fine electric wire smaller than AGW16.Information provided by Daikin Industries. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON F-302 PTFE Fine Powder Processing Methods: Paste extrusion.Applications: Small to large diameter tubes, flexible hoses, shrinkable tubes, heavy duty electric wires smaller than AGW18, and jackets.Information provided by .. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON M-111 PTFE Molding Powder, Fine Cut Fine cut powder.Processing Methods: Compression molding.Features: Produces moldings with extremely smooth and fine surface. Suited to making packing and gaskets since moldings have an especially go.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON M-12 PTFE Molding Powder, Fine Cut Fine cut powder.Processing Methods: Compression molding.Features: Useful in making products requiring fine texture, especially insulation skiving tapes. Also allows uniform mixing of inorganic fill.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON M-139 PTFE Molding Powder, Free Flow Free flow powder.Processing Methods: Compression molding and automatic compression molding.Features: Excellent fluidity. Apparent density is large and ideal for automated compression molding proces.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON M-18 PTFE Molding Powder, Fine Cut Fine cut powder.Processing Methods: Compression molding.Features: Suited to molding of large billets, has nearly the same molding characteristics of M-12. Also allows uniform mixing of inorganic fi.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON M-392 PTFE Molding Powder, Free Flow Free flow powder.Processing Methods: Compression molding, automatic or semi-automatic compression molding, isostatic molding, and ram extrusion.Features: Good fill characteristics particularly into .. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON MG-1030 PTFE 15% Glass Fiber Filled Molding Powder 15% glass fiber filled. High wear resistance, low friction, good electrical properties.Applications: Mechanical and electrical service. Available in all forms (e.g. bearings, gaskets, valve seats,.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON MG-1050F PTFE 25% Glass Fiber Filled Molding Powder, High Apparent Density, Free Flow 25% glass fiber filled. High apparent density and free-flowing properties. High wear resistance, low friction, good electrical properties.Applications: Mechanical and electrical service. Availabl.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON MG-1241 PTFE 20% Glass Fiber and 5% Graphite Filled Molding Powder 20% glass fiber and 5% graphite filled. High wear resistance, low friction, high creep resistance.Applications: Mechanical and chemical service (e.g. piston rings, bearing pads, and packings)Inform.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON MG-1241F PTFE 20% Glass Fiber and 5% Graphite Filled Molding Powder, High Apparent Density, Free Flow 20% glass fiber and 5% graphite filled. High apparent density and free-flowing properties. High wear resistance, low friction, high creep resistance.Applications: Mechanical and chemical service (.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON MG-1431 PTFE 15% Glass Fiber and 5% MoS2 Filled Molding Powder 15% glass fiber and 5% MoS2 filled. High wear resistance, good electrical properties, low friction, high creep resistance.Applications: Mechanical and electrical service (e.g. split-curled bearings.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON MG-1431F PTFE 20% Glass Fiber and 5% MoS2 Filled Molding Powder, High Apparent Density, Free Flow 15% glass fiber and 5% MoS2 filled. High apparent density and free-flowing properties. High wear resistance, good electrical properties, low friction, high creep resistance.Applications: Mechanica.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON MG-2030 PTFE 15% Graphite Filled Molding Powder 15% graphite filled. Low friction, excellent chemical resistance, high creep resistance.Applications: Mechanical and chemical service (e.g. bearings, gaskets, packings)Information provided by Daiki.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON MG-2060 PTFE 30% Graphite Filled Molding Powder 30% graphite filled. Low friction, excellent chemical resistance, high creep resistance.Applications: Mechanical and chemical service (e.g. bearings, gaskets, packings)Information provided by Daiki.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON MG-6030 PTFE 15% Carbon Fiber Filled Molding Powder 15% carbon fiber filled. High wear resistance, high load resistance, high bend resistance.Applications: Mechanical service (e.g. bearings, mechanical seals and bearing pads)Information provided by .. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON MG-6030F PTFE 15% Carbon Fiber Filled Molding Powder, High Apparent Density, Free Flow 15% carbon fiber filled. High apparent density and free-flowing properties. High wear resistance, high load resistance, high bend resistance.Applications: Mechanical service (e.g. bearings, mechan.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin POLYFLON MG-6050 PTFE 25% Carbon Fiber Filled Molding Powder 25% carbon fiber filled. High wear resistance, high load resistance, high bend resistance.Applications: Mechanical service (e.g. bearings, mechanical seals and bearing pads)Information provided by .. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin NEOFLON AP-201 PFA Pellets NEOFLON PFA pellets have good melt flowability, and can be processed in the same manner as other thermoplastic resins.Applications: Complicated injection molded parts requiring high melt flow to fil.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin NEOFLON NP-20 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding, injection molding.Applications: Wire and cable coatings, films,.. |
|||
Compressive Strength | 5.00 - 6.00 MPa @Temperature 25.0 °C |
725 - 870 psi @Temperature 77.0 °F |
1% deformation; ASTM D695 |
Daikin NEOFLON NP-3000 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion.Applications: Ultra high speed wire and cable coatings.Information provi.. |