Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 48.0 - 51.0 MPa | 6960 - 7400 psi | |
Pyrotek Dense Fused Silica Pre-Cast Shapes Pyrocast Dense Fused Silica is an economical product for shapes demanding thermal shock resistance at temperatures. Pyrocast DFS stands up to repeated use in molten metal casting in aluminum, coppe.. |
|||
Compressive Strength | 48.0 MPa | 6960 psi | with grain |
Pyrotek PT-10 Graphite PT-10 Graphite offers the highest resistance to oxidation available. Its unique composition gives it the most durable, long lasting, oxidation resistant properties available from treated graphite.A.. |
|||
Compressive Strength | 48.0 MPa | 6960 psi | cured at 540°C |
Pyrotek Pyrocast AR-S Castable Refractory Pyrocast AR-S is a low cement, fused silica, castable refractory which exhibits excellent resistance to thermal shock. It is inert to liquid aluminum and its alloys. It is a high strength material.. |
|||
Compressive Strength | 48.0 MPa | 6960 psi | 5% pressing; EN ISO 604 |
Schwartz Technical Plastics LAMIGAMID® 317 Cast Polyamide 6, Heat Stabilized, Conditioned Application: coupling parts, sealing rings, bearingsInformation provided by Schwartz Technical Plastics GmbH |
|||
Compressive Strength | 48.0 MPa | 6960 psi | 5% pressing; EN ISO 604 |
Schwartz Technical Plastics LAMIGAMID® 317 Cast Polyamide 6, Heat Stabilized, Dry Application: coupling parts, sealing rings, bearingsInformation provided by Schwartz Technical Plastics GmbH |
|||
Compressive Strength | 48.0 MPa @Time 3.60e+7 sec |
6960 psi @Time 10000 hour |
|
Wolf Kunststoff ZEDEX® ZX-750V5T A9T Polymer Alloy Main Characteristics: Hard; Stiff; Tough; High dimensional stability; High fatigue strength; High weather resistance; Good fire behavior; Suitable for vacuum; Good machinability; Contains PTFE; Stre.. |
|||
Compressive Strength | 47.99 MPa | 6960 psi | |
CMT Materials HYTAC® C1R Highly Durable Syntactic Foam, Dust-Free Machining/Polishing HYTAC-C1R is easily machined without the dust typically associated with epoxy syntactic foam. This new copolymer base has been optimized for both the machine shop and the thermoforming process.Exce.. |