Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 85.0 MPa | 12300 psi | Cold Crushing Strength |
Gouda Vuurvast AK 90 Dense Refractory Brick Description: This brick can be used in very severe conditions, i.e. in reducing atmosphere at a high temperatures, e.g. in carbon-black furnaces.Remarks: This data represents average values, obtaine.. |
|||
Compressive Strength | 85.0 MPa | 12300 psi | ASTM D362 |
Unitika M1030B PA6, Dry Nano composite nylonInformation provided by Unitika Ltd. |
|||
Compressive Strength | 84.8 MPa | 12300 psi | |
Engineered Syntactic Systems AZ-38 Deep Water Syntactic Foam Syntactic foams are a combination of hollow spheres, a resin matrix, and other additives. When combined and processed properly, the constituents form a lightweight homogeneous material having high c.. |
|||
Compressive Strength | 85.0 MPa | 12300 psi | Absolute Drying; ASTM-D695 |
Toyobo GLAMIDE® T-803 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
Compressive Strength | 84.8 MPa | 12300 psi | ASTM D695 |
Ensinger Hydel® PC-7 Polycarbonate (PC) A polycarbonate based material with a proprietary carbon filler component. The highly dispersed filler imparts outstanding electrical consistency to minimize any hot spots. The material has good r.. |
|||
Compressive Strength | 85.0 - 100 MPa | 12300 - 14500 psi | GB/T 1040 |
Beijing Evergrow Resources Oilon Information provided by Beijing Evergrow Resources. |
|||
Compressive Strength | 84.8 - 112 MPa | 12300 - 16300 psi | |
Bulk Molding Compounds BMC T60 Grey Wear Resistant Molding Compound BMC T60 Grey is a wear resistant molding compound specifically formulated for applications that require excellent abrasion resistance. Due to its low specific gravity it has substantial cost per cu.. |
|||
Compressive Strength | 85.0 - 100 MPa | 12300 - 14500 psi | GB/T 1040 |
Beijing Evergrow Resources Enylon® Information provided by Beijing Evergrow Resources. |
|||
Compressive Strength | 85.0 - 100 MPa | 12300 - 14500 psi | GB/T 1040 |
Beijing Evergrow Resources MC Nylon Information provided by Beijing Evergrow Resources. |
|||
Compressive Strength | 84.8 - 112 MPa | 12300 - 16300 psi | |
Bulk Molding Compounds BMC T60-6006 Wear Resistant Molding Compound BMC T60-6006 is a wear resistant molding compound specifically formulated for applications that require excellent abrasion resistance. Due to its low specific gravity it has substantial cost per cu.. |