Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 64.8 MPa | 9400 psi | ASTM D638 |
Quantum Modified PPO - Noryl® Information provided by Quantum Advanced Engineering Plastics |
|||
Tensile Strength | 64.8 MPa | 9400 psi | Volume Resistivity 3 [log{ohm-cm)] |
TIMCAL ENSACO™ 350G Conductive Carbon Black ENSACO™ & SUPER P™ conductive carbon blacks are carbon blacks with a high to very high void volume allowing the retention of a carbon network at low to very low filler content. The void volume can.. |
|||
Tensile Strength | 64.8 MPa | 9400 psi | Volume Resistivity 10.3 [log{ohm-cm)] |
TIMCAL ENSACO™ 350G Conductive Carbon Black ENSACO™ & SUPER P™ conductive carbon blacks are carbon blacks with a high to very high void volume allowing the retention of a carbon network at low to very low filler content. The void volume can.. |
|||
Tensile Strength | 64.8 MPa | 9400 psi | ASTM D638 |
Ensinger Tecapeek® XP-100 Compression Molded PEEK Compound, Bearing Grade Material with 10% Graphite, 10% PTFE, and 10% Carbon Fiber Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in.. |
|||
Tensile Strength | 64.8 MPa | 9400 psi | ASTM D638 |
Aaron Industries AAROPRENE® GFABS 4010 Glass Filled Acrylonitrile-Butadiene Styrene AAROPRENE® GFABS 4000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
Tensile Strength | 64.8 MPa | 9400 psi | ASTM D638 |
Aaron Industries AAROPRENE® GFIPP 2030 High Impact Glass Filled Polypropylene AAROPRENE® GFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |