Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 483 - 621 MPa | 70000 - 90000 psi | |
Eagle Brass 200/201 Nickel Alloy, 3/4 Hardened Nickel 200/201 has properties that are useful in industries such as chemical processing and electronics. Nickel is resistant to various reducing chemicals and alkaline materials. Compared with nick.. |
|||
Tensile Strength | >= 483 MPa | >= 70000 psi | |
Eagle Brass 304L Austenitic Stainless Steel, Annealed Type 304L is a very common variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled. Lower carbon 304L minimizes chromium ca.. |
|||
Tensile Strength | >= 483 MPa | >= 70000 psi | |
Eagle Brass 305 Austenitic Stainless Steel, Annealed Type 305 is a chromium nickel stainless steel that can be spun and deep drawn more easily due to an increased nickel content that decreases work hardening. It is nonmagnetic under most conditions. .. |
|||
Tensile Strength | >= 483 MPa | >= 70000 psi | |
Eagle Brass 316L Austenitic Stainless Steel, Annealed Type 316L is an extra-low carbon version of Type 316 that minimizes carbide precipitation. Typical uses include exhaust manifolds, furnace parts, heat exchangers, jet engine parts, pharmaceutical a.. |
|||
Tensile Strength | 483 MPa | 70000 psi | As Cast |
Weartech International WT-1 Cobalt Hardfacing & Wear Resistant Alloy Applications: seaming rolls, valve seats, wear pads, pump sleeves, seals, bearings, bushings, saw blades, cuttersInformation provided by Weartech International |
|||
Tensile Strength | 483 - 621 MPa @Thickness <=25.4 mm |
70000 - 90000 psi @Thickness <=1.00 in |
Cold Drawn Bars |
Schmolz + Bickenbach IMRE™ Stainless Steel Bar Description: Ugine IMRE™ is a chromium stainless steel with improved magnetic properties used in solenoid valves. IMRE™ is at 18% chromium ferritic stainless steel with 2% Mo designed to withstand.. |