Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 1030 MPa | 150000 psi | |
Niagara LaSalle e.t.d.® 150® Cold Finished Steel Bar e.t.d.® 150® is produced from AISI medium carbon 4100 series alloy steel. The heats to be used for e.t.d. 150® are controlled to contain nitrogen in quantities normally associated with steel prod.. |
|||
Tensile Strength | 1030 MPa @Temperature -5.56 °C |
150000 psi @Temperature 22.0 °F |
Hardened and tempered to 34 HRC |
Schmolz + Bickenbach P-20 High Hard Plastic Mold Steel Description: P-20 High Hard is an improved pre-hardened mold steel that has been specially designed for large plastic molds; Material is forged on a 5000 ton press assuring maximum deformation durin.. |
|||
Tensile Strength | 1030 MPa @Temperature -5.56 °C |
150000 psi @Temperature 22.0 °F |
Hardened and tempered to 34 HRC |
Schmolz + Bickenbach P-20 Modified Plastic Mold Steel Description: P-20 Modified is an improved pre-hardened mold steel that has been specially designed for large plastic molds; The material is forged on a 5000 ton press assuring maximum deformation du.. |
|||
Tensile Strength | 1030 - 1170 MPa @Thickness >=25.4 mm |
150000 - 170000 psi @Thickness >=1.00 in |
Turned Bars |
Schmolz + Bickenbach UGIMA® 630 Stainless Steel Bar Description: 630 UGIMA® is an improved machining martensitic precipitation hardenable grade produced only by Ugitech. It is identical in every way to standard type 630 (17-4), except with respect.. |
|||
Tensile Strength | >= 1030 MPa | >= 150000 psi | |
Eagle Brass 301 Austenitic Stainless Steel, 1/2 Hardened Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens.. |
|||
Tensile Strength | >= 1030 MPa | >= 150000 psi | |
Eagle Brass 302 Austenitic Stainless Steel, 1/2 Hardened Types 302 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
Tensile Strength | >= 1030 MPa | >= 150000 psi | |
Eagle Brass 304 Austenitic Stainless Steel, 1/2 Hardened Types 304 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
Tensile Strength | >= 1030 MPa | >= 150000 psi | |
Eagle Brass 305 Austenitic Stainless Steel, 1/2 Hardened Type 305 is a chromium nickel stainless steel that can be spun and deep drawn more easily due to an increased nickel content that decreases work hardening. It is nonmagnetic under most conditions. .. |
|||
Tensile Strength | >= 1030 MPa | >= 150000 psi | |
Eagle Brass 316 Austenitic Stainless Steel, 1/2 Hardened The Mo addition increases general corrosion resistance to pitting from chloride ion solutions, and provides increased strength at elevated temperatures. Properties are similar to those of Type 304 .. |
|||
Tensile Strength | >= 1030 MPa | >= 150000 psi | |
Eagle Brass 316L Austenitic Stainless Steel, 1/2 Hardened Type 316L is an extra-low carbon version of Type 316 that minimizes carbide precipitation. Typical uses include exhaust manifolds, furnace parts, heat exchangers, jet engine parts, pharmaceutical a.. |
|||
Tensile Strength | >= 1030 MPa | >= 150000 psi | |
Eagle Brass 304L Austenitic Stainless Steel, 1/2 Hardened Type 304L is a very common variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled. Lower carbon 304L minimizes chromium ca.. |