Physical Properties | Metric | English | Comments |
---|---|---|---|
Oxygen Transmission | 65.0 cc-mm/m²-24hr-atm | 165 cc-mil/100 in²-24hr-atm | or 2600 cc/m²-atm-24 hr per 25 µm film; 38°C; 90% RH Difference |
NOVA Chemicals Sclair® 15A Butene HDPE Film Resin Film Properties. Features: Low gel, good barrier properties, strength and toughness.Applications: Lamination, co-extrusion.Data provided by the manufacturer. |
|||
Oxygen Transmission | 65.0 - 70.0 cc-mm/m²-24hr-atm | 165 - 178 cc-mil/100 in²-24hr-atm | Average value: 68.0 cc-mm/m²-24hr-atm Grade Count:4 |
Overview of materials for Polycarbonate, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Extruded". Each property range of values reported is minimum and maximum values of approp.. |
|||
Oxygen Transmission | 65.0 - 70.0 cc-mm/m²-24hr-atm | 165 - 178 cc-mil/100 in²-24hr-atm | Average value: 68.2 cc-mm/m²-24hr-atm Grade Count:3 |
Overview of materials for Polycarbonate, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Unreinforced, Flame Retardant". Each property range of values reported is minimum and max.. |
|||
Oxygen Transmission | 65.0 - 80.0 cc-mm/m²-24hr-atm | 165 - 203 cc-mil/100 in²-24hr-atm | Average value: 70.0 cc-mm/m²-24hr-atm Grade Count:12 |
Overview of materials for Polycarbonate, UV Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, UV Stabilized". Each property range of values reported is minimum and maximum values of a.. |
|||
Oxygen Transmission | 65.0 - 80.0 cc-mm/m²-24hr-atm | 165 - 203 cc-mil/100 in²-24hr-atm | Average value: 71.4 cc-mm/m²-24hr-atm Grade Count:20 |
Overview of materials for Polycarbonate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Molded". Each property range of values reported is minimum and maximum values of appropri.. |