Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 1.5 - 2.2 g/10 min @Load 5.00 kg, Temperature 190 °C |
1.5 - 2.2 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
Polyplastic Torlen® PE 2K 901 High Density Polyethylene, Carbon Filled Information provided by PolyPlastic Group. |
|||
Melt Flow | 1.8 - 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.8 - 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
NIZHNEKAMSKNEFTEKHIM PE 4116P (16402) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Melt Flow | 1.8 - 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.8 - 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
NIZHNEKAMSKNEFTEKHIM PE 4118N (18401) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Melt Flow | 1.8 - 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.8 - 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
NIZHNEKAMSKNEFTEKHIM PE 5117P (18602) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Melt Flow | 1.8 - 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.8 - 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
NIZHNEKAMSKNEFTEKHIM PE 5118P (18602) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Melt Flow | 1.8 - 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.8 - 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
NIZHNEKAMSKNEFTEKHIM PE 4115P (16402) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Melt Flow | 1.8 - 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.8 - 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
NIZHNEKAMSKNEFTEKHIM PE 4117P (18402) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Melt Flow | 1.8 - 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.8 - 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
NIZHNEKAMSKNEFTEKHIM PE 4118P (18402) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |