Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 18 - 24 g/10 min @Load 11.6 kg, Temperature 250 °C |
18 - 24 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
Polymer Resources PPX-GP3-[color]-HF Modified-PPO, General Purpose, High Flow Modified-Polyphenylene Oxide, General Purpose, High Flow, 235F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sample.. |
|||
Melt Flow | 20 - 24 g/10 min @Load 1.20 kg, Temperature 300 °C |
20 - 24 g/10 min @Load 2.65 lb, Temperature 572 °F |
|
Kazanorgsintez PC-022 Polycarbonate Production Method: Obtained by means of polycondensation method. Application: Intended for product manufacture by method of die-casting.Information Provided by Kazanorgsintez |
|||
Melt Flow | 18 - 24 g/10 min @Load 2.16 kg, Temperature 190 °C |
18 - 24 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem PCC 2314 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
Melt Flow | 18 - 24 g/10 min @Load 2.16 kg, Temperature 190 °C |
18 - 24 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem PH 1710 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
Melt Flow | 18 - 24 g/10 min @Load 2.16 kg, Temperature 190 °C |
18 - 24 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem PH 1721 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
Melt Flow | 16 - 24 g/10 min @Temperature 230 °C |
16 - 24 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ PP 1579 Impact Grade Polypropylene DescriptionPolyfort® PP 1579H is an impact grade of polypropylene for use in parts which require good impact and good appearance in light-weight injection molded parts. Information provided by A. .. |
|||
Melt Flow | 16 - 24 g/10 min @Load 2.16 kg, Temperature 230 °C |
16 - 24 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman... |
|||
Melt Flow | 16 - 24 g/10 min @Temperature 230 °C |
16 - 24 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ PP 1579 Impact Grade Polypropylene DescriptionPolyfort® PP 1579H is an impact grade of polypropylene for use in parts which require good impact and good appearance in light-weight injection molded parts. Information provided by A. .. |
|||
Melt Flow | 16 - 24 g/10 min @Load 2.16 kg, Temperature 230 °C |
16 - 24 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman... |
|||
Melt Flow | 16 - 24 g/10 min @Temperature 230 °C |
16 - 24 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1498HU is a high flow UV stabilized medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. .. |
|||
Melt Flow | 16 - 24 g/10 min @Temperature 230 °C |
16 - 24 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ PP 1579 Impact Grade Polypropylene DescriptionPolyfort® PP 1579H is an impact grade of polypropylene for use in parts which require good impact and good appearance in light-weight injection molded parts. Information provided by A. .. |
|||
Melt Flow | 16 - 24 g/10 min @Load 2.16 kg, Temperature 230 °C |
16 - 24 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman... |
|||
Melt Flow | 16 - 24 g/10 min @Temperature 230 °C |
16 - 24 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1498HU is a high flow UV stabilized medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. .. |
|||
Melt Flow | 16 - 24 g/10 min @Temperature 230 °C |
16 - 24 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ PP 1579 Impact Grade Polypropylene DescriptionPolyfort® PP 1579H is an impact grade of polypropylene for use in parts which require good impact and good appearance in light-weight injection molded parts. Information provided by A. .. |
|||
Melt Flow | 16 - 24 g/10 min | 16 - 24 g/10 min | ASTM D1238 |
Westlake Epolene® C-17 Coating Grade - Highly Branched Medium Molecular Weight Polyethylene Polymer Product Description: Epolene C-17 is a branched low density polyethylene with a relatively high melt point and viscosity compared to other Epolene C-type Polymers. It is useful to modify paraffin wa.. |
|||
Melt Flow | 16 - 24 g/10 min | 16 - 24 g/10 min | 72-412 |
Westlake Epolene® C-17P Coating Grade - Branched Medium Molecular Weight Polyethylene Polymer Description: Epolene C-17P is a branched low density polyethylene powder with a relatively high melt point and viscosity compared to other Epolene C-type Polymers. It is useful to modify paraffin wa.. |
|||
Melt Flow | 16 - 24 g/10 min @Load 2.16 kg, Temperature 230 °C |
16 - 24 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman... |
|||
Melt Flow | 16 - 24 g/10 min @Temperature 230 °C |
16 - 24 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1498HU is a high flow UV stabilized medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. .. |
|||
Melt Flow | 16 - 24 g/10 min @Temperature 230 °C |
16 - 24 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1498HU is a high flow UV stabilized medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. .. |
|||
Melt Flow | 16 - 24 g/10 min @Temperature 230 °C |
16 - 24 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ PP 1579 Impact Grade Polypropylene DescriptionPolyfort® PP 1579H is an impact grade of polypropylene for use in parts which require good impact and good appearance in light-weight injection molded parts. Information provided by A. .. |
|||
Melt Flow | 16 - 24 g/10 min @Temperature 230 °C |
16 - 24 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ PP 1579 Impact Grade Polypropylene DescriptionPolyfort® PP 1579H is an impact grade of polypropylene for use in parts which require good impact and good appearance in light-weight injection molded parts. Information provided by A. .. |
|||
Melt Flow | 16 - 24 g/10 min @Load 2.16 kg, Temperature 230 °C |
16 - 24 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman... |
|||
Melt Flow | 18 - 24 g/10 min @Load 10.0 kg, Temperature 240 °C |
18 - 24 g/10 min @Load 22.0 lb, Temperature 464 °F |
ISO 1133 |
Cossa Polimeri ESTABLEND PA 2500 ABS / Nylon 6 Blend ESTABLEND PA is a blend of acrylonitrile butadiene styrene and polyamide 6.Easy processing, high surface quality, high chemical resistance, good heat resistanceInformation provided by Cossa Polimeri.. |
|||
Melt Flow | 18 - 24 g/10 min | 18 - 24 g/10 min | ASTM D1238 |
Buckeye Polymers BP PPC 0220 BLK Polypropylene Copolymer Product Information: Black Polypropylene Copolymer good for general purpose programs requiring moderate impact resistance.Product Features:Good impact resistanceGood UV resistanceGood chemical resis.. |
|||
Melt Flow | 18 - 24 g/10 min | 18 - 24 g/10 min | ASTM D1238 |
Buckeye Polymers BP RPPC 1020 TU BLK Polypropylene Copolymer Product Information: Black Polypropylene Copolymer good for general purpose programs requiring moderate impact resistance.Product Features:Good impact resistanceGood UV resistanceGood chemical resis.. |
|||
Melt Flow | 22 - 24 g/10 min @Load 2.16 kg, Temperature 230 °C |
22 - 24 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Samyang Triel® 5300 Thermoplastic Polyether Ester Elastomer TRIEL® resins offer superior mechanical properties, elasticities, heat and chemical resistance, which allow it to be widely used for electric/electronic equipments, automotive parts and outdoor rec.. |
|||
Melt Flow | 18 - 24 g/10 min | 18 - 24 g/10 min | ASTM D1238 |
Buckeye Polymers BP PPC 0218-22 BLK Polypropylene Copolymer Product Information: Black Polypropylene Copolymer good for general purpose programs requiring moderate impact resistance. Meets or exceeds all properties associated with GMP.PP.086R.Product Featur.. |
|||
Melt Flow | 18 - 24 g/10 min | 18 - 24 g/10 min | ASTM D1238 |
Buckeye Polymers BP RPPC 1720 TURXF Polypropylene, Talc Filled Product Information: Our Talc filled product lines exhibit excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and .. |
|||
Melt Flow | 16 - 24 g/10 min @Temperature 230 °C |
16 - 24 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1498HU is a high flow UV stabilized medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. .. |