Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 6.4 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.4 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics Lexan® ML4248 PC Polycarbonate for aircraft applications requiring FAR 25.853a compliance. Extrusion grade. Transparent, transluscent and opaque colors. |
|||
Melt Flow | 6.4 g/10 min | 6.4 g/10 min | Exxon Method |
ExxonMobil Escorene® LD-769 High EVA Compounding Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 28% vinyl acetate copolymer designed for high filler acceptance. Compounds produced from this resin have excellent flexibility and toughness.Appl.. |
|||
Melt Flow | 6.4 - 9.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.4 - 9.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem HC 7260 HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce .. |
|||
Melt Flow | 6.4 - 9.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.4 - 9.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem HC 7260 LS HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce .. |
|||
Melt Flow | 6.4 - 9.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.4 - 9.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem HC 7260 LS-L HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce .. |
|||
Melt Flow | 6.4 g/10 min @Load 10.0 kg, Temperature 250 °C |
6.4 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
SABIC Innovative Plastics NORYL STN15 PPE+HIPS (Asia Pacific) PPE+HIPS Unfilled Auto Interior |
|||
Melt Flow | 6.4 g/10 min @Load 6.60 kg, Temperature 295 °C |
6.4 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D 1238 |
SABIC Innovative Plastics Ultem ATX100R PEI+PCE Higher impact, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 HB listing.This data was supplied by SABIC-IP for the Americas region. |
|||
Melt Flow | 6.4 g/10 min @Load 6.60 kg, Temperature 295 °C |
6.4 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D 1238 |
SABIC Innovative Plastics Ultem ATX100R PEI+PCE (Asia Pacific) Higher impact, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 HB listing.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Melt Flow | 6.4 g/10 min @Load 5.00 kg, Temperature 300 °C |
6.4 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics NORYL IGN5531 PPE+PS Noryl* IGN5531 is an 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Nor.. |
|||
Melt Flow | 6.4 g/10 min @Load 5.00 kg, Temperature 300 °C |
6.4 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics NORYL IGN5531 PPE+PS (Asia Pacific) Noryl* IGN5531 is an 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Nor.. |
|||
Melt Flow | 6.4 g/10 min @Load 5.00 kg, Temperature 300 °C |
6.4 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics NORYL IGN5531 PPE+PS (Europe-Africa-Middle East) Noryl* IGN5531 is an 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Nor.. |
|||
Melt Flow | 6.4 g/10 min @Load 2.20 kg |
6.4 g/10 min @Load 4.86 lb |
ASTM D1238 |
Sumitomo Chemical ESPOLEX® 903 Thermoplastic Elastomer ESPOLEX® TPE Series is a group of thermoplastic elastomers produced by Sumitomo Chemical Company. Among its material advantages, ESPOLEX® TPE Series is distinguished by offering many low-densi.. |
|||
Melt Flow | 6.4 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.4 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont Bynel® 1123 Modified EVA Adhesive Resin Bynel® Series 1100 resins are modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylen.. |
|||
Melt Flow | 6.4 g/10 min | 6.4 g/10 min | ASTM D1238 |
Dow 751A Low Density Polyethylene Resin A high additive film resin for general packaging applications For cast film extrusion A fast blooming resin for high speed bag conversion Complies with U.S. FDA 21 CFR 177.1520 (c) 2.1 Information p.. |