Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Index of Compound | <= 1.5 g/10 min @Load 5.00 kg, Temperature 190 °C |
<= 1.5 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
Polykemi AB POLYelast TPE Z706EX Thermoplastic Elastomer, SEBS-based Information provided by Polykemi AB |
|||
Melt Index of Compound | 1.5 g/10 min | 1.5 g/10 min | ASTM D1238 |
DuPont Elvax® 462 Ethylene-Vinyl Acetate Copolymer Resin
(discontinued **) Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Melt Index of Compound | 1.5 g/10 min @Temperature 190 °C |
1.5 g/10 min @Temperature 374 °F |
ASTM D1238 |
Mitsui ADMER® NF488A PE Type Polyolefin ADMER® Adhesive Resin is a modified polyolefin with functional groups, designed to bond to a variety of polyolefins, ionomers, polyamides, ethylene vinyl alcohol (EVOH), polyesters (PET), polycar.. |
|||
Melt Index of Compound | 1.5 g/10 min | 1.5 g/10 min | ASTM D1238 |
Lushan M-1 Adhesive Resin for Barrier Container and Tube Adhesive resin Lushan series for barrier container and tube is used for bonding a wide variety of materials, It’s most often used to adhering PE and EVOH, PP and EVOH, etc. Adhesive resins Lush.. |
|||
Melt Index of Compound | 1.5 - 2.4 g/10 min | 1.5 - 2.4 g/10 min | |
Sibur 21020-PM1 Polypropylene with Low Haze For production of three-layer PE/PP film, for production of sheets for cups and thin casting. It is allowed for contact with food products. |
|||
Melt Index of Compound | 1.5 g/10 min @Load 21.6 kg, Temperature 150 °C |
1.5 g/10 min @Load 47.6 lb, Temperature 302 °F |
Fainplast |
Fainplast Compounds HAX HF 019/G Halogen Free PVC Sheathing; high flexibility |
|||
Melt Index of Compound | 1.5 - 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.5 - 2.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Arkema Group LOTRYL® 30 BA 02 Copolymer Ethylene - Butyl Acrylate LOTRYL® 30 BA 02 is a random copolymer of ethylene and butyl acrylate, prepared by the high pressure polymerization process. LOTRYL® 30 BA 02 is used for polymer modification, in compounds formula.. |
|||
Melt Index of Compound | 1.5 - 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.5 - 2.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Arkema Group OREVAC® 9314 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |