Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage | 0.011 - 0.0125 cm/cm @Thickness 3.17 mm |
0.011 - 0.0125 in/in @Thickness 0.125 in |
|
Ovation Polymers Nima™ NH PA66UT Nylon 66 Polyamide 66 - Ultra Tough, Flame Retarded Non-Hal grade with excellent retention of mechanical properties. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humi.. |
|||
Linear Mold Shrinkage | 0.011 - 0.0125 cm/cm @Thickness 3.17 mm |
0.011 - 0.0125 in/in @Thickness 0.125 in |
|
Ovation Polymers Opnyl OP66UT108 Nylon 66 Ultra Tough - High Impact, Excellent retention of mechanical properties, High service temperature. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All.. |
|||
Linear Mold Shrinkage | 0.011 - 0.0125 cm/cm @Thickness 3.17 mm |
0.011 - 0.0125 in/in @Thickness 0.125 in |
|
Ovation Polymers Opnyl OP66UT119 Nylon 66 Ultra Tough - High Impact, Excellent retention of mechanical properties, High service temperature. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All.. |
|||
Linear Mold Shrinkage | 0.000500 - 0.0125 cm/cm | 0.000500 - 0.0125 in/in | Average value: 0.00805 cm/cm Grade Count:21 |
Overview of materials for Thermoset Polyurethane, Adhesive This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Adhesive". Each property range of values reported is minimum and maximum values .. |