Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.0190 - 0.100 g/cc | 0.000686 - 0.00361 lb/in³ | Pressurized batch pre-foamer; Usual Use |
NOVA Chemicals Gedexcel® 54B Expandable Polystyrene Styrene homopolymer containing pentane, used as a blowing agent. Fast molding cycle product and reduced stabilization time in silo. Especially adapted to high density molding and thin thickness, an.. |
|||
Density | 0.0190 - 0.0400 g/cc | 0.000686 - 0.00145 lb/in³ | Pressurized batch pre-foamer; Usual Use |
NOVA Chemicals Gedexcel® 54XA Expandable Polystyrene Styrene homopolymer containing pentane, used as a blowing agent with an additive improving its reaction to fire. Fast molding cycle product to obtain mechanical properties for form molding parts wit.. |
|||
Density | 0.0190 - 0.0400 g/cc | 0.000686 - 0.00145 lb/in³ | Density range normally used |
Polimeri Europa Extir® B 2000 Expandable Polystyrene, Fast Molding
(discontinued **) Particle size range is 0.4 - 0.75 mm. Minimum apparent density on a discontinuous pre-expander is 18 g/l.Processing technology used for Type B 2000 is: Molding, Vacuum.Specific characteristics: Goo.. |
|||
Density | 0.0190 - 0.0350 g/cc | 0.000686 - 0.00126 lb/in³ | Density range normally used |
Polimeri Europa Extir® PD D 2000 AE Expandable Polystyrene, Fast Molding Flame Retardant
(discontinued **)< Particle size range is 0.4 - 0.75 mm. Minimum apparent density on a discontinuous pre-expander is 18 g/l. Minimum apparent density on a continuous pre-expander is 20 g/l.Processing technology used.. |
|||
Density | >= 0.0190 g/cc | >= 0.000686 lb/in³ | Minimum achievable; Single stage pre-expansion in continuous expander at atmospheric pressure |
Ineos Nova Styrocell® M742C Expandable Polystyrene A high strength regular molding grade consisting of spherical polystyrene beads containing pentane as expansion agent, typically used for medium density foam.Applications: Styrocell M742C is used ma.. |
|||
Density | 0.0190 - 0.0400 g/cc | 0.000686 - 0.00145 lb/in³ | Normal molded density assuming cost optimized selection of processing conditions. |
Ineos Nova Styrocell® M742C Expandable Polystyrene A high strength regular molding grade consisting of spherical polystyrene beads containing pentane as expansion agent, typically used for medium density foam.Applications: Styrocell M742C is used ma.. |
|||
Density | 0.0190 g/cc | 0.000686 lb/in³ | 45 second cycle time |
Jackon JACKOCELL® S214 Expanded Polystyrene Construction and Block Molding Pre-ExpansionThe unique design of polystyrene chains and additive chemistry in Jackocell® S214 gives pre-expanded beads high dimensional stability even at low densities, which typically reduces a.. |
|||
Density | 0.0190 g/cc | 0.000686 lb/in³ | core density |
Ultracor® UKF-85-1/4-1.5 Honeycomb Core Material Construction: ±45° K49 108. Fiber: Kevlar® K49. Ultracor® is a very low density honeycomb core material designed for use in highly weight-sensitive structures. It is expected that it will be.. |
|||
Density | 0.0190 - 0.0250 g/cc | 0.000686 - 0.000903 lb/in³ | sheet density |
Zotefoams Plastazote® LD23 Low Density Polyethylene Foam Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Density | 0.0190 - 0.0260 g/cc | 0.000686 - 0.000939 lb/in³ | sheet density |
Zotefoams Plastazote® LD24FM Low Density Polyethylene Foam, Flame Retarded Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Density | 0.0190 - 0.0260 g/cc | 0.000686 - 0.000939 lb/in³ | sheet density |
Zotefoams Plastazote® LD24FMSV Low Density Polyethylene Foam, Flame Retarded Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Density | 0.0190 - 0.0250 g/cc | 0.000686 - 0.000903 lb/in³ | sheet density |
Zotefoams Plastazote® LD24LC Low Density Polyethylene Foam, Large Cell Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Density | 0.0190 - 0.0250 g/cc | 0.000686 - 0.000903 lb/in³ | sheet density |
Zotefoams Plastazote® LD24MC Low Density Polyethylene Foam, Medium Cell Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Density | 0.0190 - 0.0250 g/cc | 0.000686 - 0.000903 lb/in³ | sheet density |
Zotefoams Plastazote® LD24 Low Density Polyethylene Foam Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Density | 0.0190 - 0.0350 g/cc | 0.000686 - 0.00126 lb/in³ | Density range normally used |
Polimeri Europa Extir® C 3000 Expandable Polystyrene, Fast Molding
(discontinued **) Particle size range is 0.7 - 1 mm. Minimum apparent density on a discontinuous pre-expander is 18 g/l.Processing technology used for Type C 3000 is: Molding, Vacuum.Specific characteristics: High t.. |