Zotefoams Plastazote® LD45 Low Density Polyethylene Foam

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Zotefoams
Trade Name	Plastazote®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zotefoams Plastazote® LD45 Low Density Polyethylene Foam.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact and US FDA regulations.Information provided by Zotefoams

Physical Properties	Metric	English	Comments
Density	0.0370 - 0.0470 g/cc	0.00134 - 0.00170 lb/in³	sheet density
	0.0450 g/cc	0.00163 lb/in³	Nominal skin/skin; BS ISO 7214 1998
Cell Length	0.400 mm	0.0157 in	Typical Diameter
	0.250 - 0.600 mm	0.00984 - 0.0236 in

Mechanical Properties	Metric	English	Comments
Hardness, Shore OO	60	60	10 mm cell/cell thickness; ISO 868 1985
Tensile Strength	0.560 MPa	81.2 psi	ISO 7214 1998
Elongation at Break	175 %	175 %
Flexural Modulus	0.00100 GPa	0.145 ksi	BS4370, part 4, method 14
Compressive Yield Strength	0.0770 MPa @Strain 10.0 %	11.2 psi @Strain 10.0 %	BS ISO 7214 1998
	0.0940 MPa @Strain 25.0 %	13.6 psi @Strain 25.0 %	BS ISO 7214 1998
	0.130 MPa @Strain 40.0 %	18.9 psi @Strain 40.0 %	BS ISO 7214 1998
	0.170 MPa @Strain 50.0 %	24.7 psi @Strain 50.0 %	BS ISO 7214 1998
Tear Strength	1.15 kN/m	6.56 pli	BS EN ISO 8067 1995
Compression Set	2.5 % @Time 79200 sec, Strain 25.0 %	2.5 % @Time 22.0 hour, Strain 25.0 %	24 hr recovery; BS ISO 7214 1998
	7.5 % @Time 79200 sec, Strain 25.0 %	7.5 % @Time 22.0 hour, Strain 25.0 %	0.5 hr recovery; BS ISO 7214 1998
	10 % @Time 79200 sec, Strain 50.0 %	10 % @Time 22.0 hour, Strain 50.0 %	24 hr recovery; BS ISO 7214 1998
	18.5 % @Time 79200 sec, Strain 50.0 %	18.5 % @Time 22.0 hour, Strain 50.0 %	0.5 hr recovery; BS ISO 7214 1998

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.0420 W/m-K	0.291 BTU-in/hr-ft²-°F	mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air	105 °C	221 °F
Minimum Service Temperature, Air	-70.0 °C	-94.0 °F
Flammability Test	0.70 @Thickness 13.0 mm	0.70 @Thickness 0.512 in	Horizontal Burn Rate, mm/sec; ISO 7214 1998
	1.3 @Thickness 5.00 mm	1.3 @Thickness 0.197 in	Horizontal Burn Rate, mm/sec; ISO 7214 1998
Shrinkage	<= 1.0 % @Temperature 70.0 °C	<= 1.0 % @Temperature 158 °F
	<= 2.0 % @Temperature 80.0 °C	<= 2.0 % @Temperature 176 °F
	<= 3.0 % @Temperature 90.0 °C	<= 3.0 % @Temperature 194 °F