Zircar Ceramics Z-MAG-B Non-RCF Blanket

Category	Ceramic , Oxide , Silicon Oxide
Manufacturer	Zircar Ceramics
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zircar Ceramics Z-MAG-B Non-RCF Blanket.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Mechanically needled silica magnesia fiber blanket provides much of the same performance found in ceramic fiber blanket but in a NON RCF composition.Information provided by Zircar Ceramics.

Physical Properties	Metric	English	Comments
Density	2.54 g/cc	0.0918 lb/in³
Filament Diameter	4.0 µm	4.0 µm

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	0.0350 MPa	5.08 psi	Perpendicular to Thickness; ASTM 686-76
Compression Set	78 %	78 %	50% Compression, Parallel
	89 %	89 %	30% Compression, Parallel
	96 %	96 %	10% Compression, Parallel

Thermal Properties	Metric	English	Comments
Insulation R Value	101 @Thickness 254 mm, Temperature 1100 °C	101 @Thickness 10.0 in, Temperature 2010 °F	Cold Face Temp, °C; 8 pcf density blanket
	114 @Thickness 203 mm, Temperature 1100 °C	114 @Thickness 8.00 in, Temperature 2010 °F	Cold Face Temp, °C; 8 pcf density blanket
	168 @Thickness 102 mm, Temperature 1100 °C	168 @Thickness 4.00 in, Temperature 2010 °F	Cold Face Temp, °C; 8 pcf density blanket
	243 @Thickness 50.8 mm, Temperature 1100 °C	243 @Thickness 2.00 in, Temperature 2010 °F	Cold Face Temp, °C; 8 pcf density blanket
	338 @Thickness 25.4 mm, Temperature 1100 °C	338 @Thickness 1.00 in, Temperature 2010 °F	Cold Face Temp, °C; 8 pcf density blanket
Melting Point	1500 °C	2730 °F
Maximum Service Temperature, Air	1260 °C	2300 °F
Shrinkage	1.70 % @Temperature 1000 °C, Time 90000 sec	1.70 % @Temperature 1830 °F, Time 25.0 hour	8 pcf blanket (Perpendicular to Thickness)
	3.00 % @Temperature 1260 °C, Time 90000 sec	3.00 % @Temperature 2300 °F, Time 25.0 hour	8 pcf blanket (Perpendicular to Thickness)

Component Elements Properties	Metric	English
MgO	19 - 26 %	19 - 26 %
Other	0.00 - 4.0 %	0.00 - 4.0 %
SiO2	72 - 77 %	72 - 77 %

Descriptive Properties	Value	Comments
Color	Bluish White