Westlake EBAC® SP1806 17.5%, Ethylene-Methyl Acrylate Copolymer

Category	Polymer , Thermoplastic , Ethylene Butyl Acrylate
Manufacturer	Westlake Chemical Corporation
Trade Name	EBAC®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Westlake EBAC® SP1806 17.5%, Ethylene-Methyl Acrylate Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Westlake EBAC® SP1806 is an ethylene butyl acrylate copolymer designed for extrusion coating and laminating. SP1806 can also be compounded as an impact modifier or used in highly filled applications. Westlake EBAC® resins are less crystalline and softer than polyethylene and offer compatibility and adhesion to typically difficult to bond to polymers. SP1806 is non-corrosive at extrusion temperatures and has excellent thermal stability.Key Attributes:Good adhesion/compatibility to various substratesGood heat and RF sealingLow temperature toughnessSoft, flexible, tough without plasticizerApplication/Uses: Extrusion coating / laminationsFlexible PackagingImpact ModifierCompounding / high filler loadingsInformation provided by Westlake Chemical

Physical Properties	Metric	English	Comments
Density	0.925 g/cc	0.0334 lb/in³	ASTM D1505
Butyl Acrylate Content	17.5 %	17.5 %	Westlake
Melt Flow	7.3 g/10 min @Load 2.16 kg, Temperature 190 °C	7.3 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	40	40	ASTM D2240
Tensile Strength at Break	10.0 MPa	1450 psi	50 mm/min; ASTM D 638 Type IV Specimen
Elongation at Break	730 %	730 %	50 mm/min; ASTM D 638 Type IV Specimen

Thermal Properties	Metric	English	Comments
Melting Point	91.0 °C	196 °F	by DSC; ASTM D3418
Vicat Softening Point	55.0 °C	131 °F	ASTM D1525
Brittleness Temperature	<= -73.0 °C	<= -99.4 °F	ASTM D746

Descriptive Properties	Value	Comments
Process	Coating
	Extrusion
Region	US & Canada	Bamberger Polymers Distribution