Trelleborg R398 Commercial Natural Rubber Polyisoprene
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Trelleborg |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Trelleborg R398 Commercial Natural Rubber Polyisoprene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
All information provided by Trelleborg
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 35 | 35 | |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | |
| Elongation at Break | 700 % | 700 % | |
| Tear Strength | 30.0 kN/m | 171 pli | |
| Abrasion | 60 | 60 | mm<sup>3</sup>; 5 N Load |
| Compression Set | 30 % @Temperature 70.0 °C, Time 79200 sec |
30 % @Temperature 158 °F, Time 22.0 hour |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Green |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4701-40-30 Cellular Urethane Foam
- Quadrant EPP Nylatron® GS PA 6 + MoS2, extruded (ISO Data)
- Flint Hills PP 13R9A Random Copolymer Polypropylene
- Taiwan PU Corporation TPUI-L85 Low Temperature Resistance, Injection Molding Polyester Base TPU
- A. Schulman POLYBLAK™ 4669 Premium Conductive 35% Carbon Black Concentrate Based In LLDPE
- Total MDPE HT 514 Medium Density Polyethylene, Blown Film
- Dandong Taico Minerals TAICOCITE® TC8 Magnesium Hydroxide
- Ensinger PVC Polyvinylchloride (PVC)
- ExxonMobil Escorene® UL-7760 EVA Copolymer, Adhesive and Sealant Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved