Toyobo Vylopet® EMC310K Glass Reinforced Polyester, Easy Molding Grade
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | Toyobo |
| Trade Name | VYLOPET® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo Vylopet® EMC310K Glass Reinforced Polyester, Easy Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Feature: HB UL-94 classApplications: General componentsGeneral features of Vylopet® include heat resistance, good mechanical properties, high dielectric strength and tracking resistance, chemical & weather resistance, and processability.Information provided by Toyobo Co., Ltd
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 91 | 91 | ASTM D785 |
| Tensile Strength, Ultimate | 101 MPa | 14600 psi | ASTM D638 |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638 |
| Flexural Yield Strength | 147 MPa | 21300 psi | ASTM D790 |
| Flexural Modulus | 7.30 GPa | 1060 ksi | ASTM D790 |
| Compressive Yield Strength | 96.0 MPa | 13900 psi | ASTM D695 |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 33 | 33 | ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 °C | 491 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| UL RTI, Electrical | 120 °C | 248 °F | UL-746B |
| Flammability, UL94 | HB @Thickness 0.7937 mm |
HB @Thickness 0.03125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 135 sec | 135 sec | ASTM D495 |
| Comparative Tracking Index | 280 V | 280 V | IEC test |
Users viewing this material also viewed the following:
- Lubriplate SFL-0 Aluminum Complex Synthetic Food Machinery Grade Grease
- KKPC Kuhmo HFH 403 Flame Retarded HIPS
- Techmer ES HiFill® PA6 GF14 L 14% Glass Filled
- A. Schulman POLYBATCH™ Blue 4500GZ Concentrate Based in Low-Density Polyethylene
- Wanhua Chemical Wanthane® WHT-6236 TPU Hot-Melt Adhesive
- Zeus PFA Tubing
- Ensinger Tecapeek® XP-99 Compression Molded PEEK Compound, Bearing Grade Material with 7% Graphite, 8% PTFE, and 15% Carbon Fiber
- ConocoPhillips Hydroclear® 100 Turbine Oil
- 3M Scotchcal™ ElectroCut™ 7125-88 Graphic Film
- Beijing Evergrow Resources Rayon Activated Carbon
Copyright © lookpolymers.com All Rights Reserved