Toyobo PELPRENE™ P40U Polyester TPE, Weather-resistant
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo PELPRENE™ P40U Polyester TPE, Weather-resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Polyester TPE, Weather-resistantInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.48 % | 0.48 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.0050 cm/cm @Thickness 2.00 mm |
0.0050 in/in @Thickness 0.0787 in |
|
| Melt Index of Compound | 10 g/10 min @Temperature 190 °C |
10 g/10 min @Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 89 | 89 | JIS K6301 |
| Hardness, Shore D | 38 | 38 | ASTM D2240 |
| Tensile Strength at Break | 23.0 MPa | 3340 psi | ASTM D638 |
| Elongation at Break | 690 % | 690 % | ASTM D638 |
| 50% Modulus | 0.00640 GPa | 0.928 ksi | ASTM D638 |
| Flexural Modulus | 0.0510 GPa | 7.40 ksi | ASTM D790 |
| Compressive Modulus | 0.00460 GPa | 0.667 ksi | 0.1; ASTM D695 |
| Resilience | 78 | 78 | JIS K6301 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tear Strength | 98.0 kN/m | 559 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 20 | 20 | ASTM D1044 |
| Compression Set | 50 % | 50 % | JIS K6301 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 170 µm/m-°C @Temperature 20.0 °C |
94.4 µin/in-°F @Temperature 68.0 °F |
TMA |
| Melting Point | 172 °C | 342 °F | By DSC |
| Maximum Service Temperature, Air | <= 25.0 °C | <= 77.0 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Vicat Softening Point | 120 °C | 248 °F | ASTM D1525 |
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | JIS K6301 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+12 ohm-cm | 2.00e+12 ohm-cm | ASTM D257 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | JIS K2111 |
Users viewing this material also viewed the following:
- Hong Kun Group UV 234 UV Absorber
- Ferro IP 760 Passivation Glasses (Pb-B-Si-Al; Pb-Si-Al; Si-Pb-Al Silicates)
- Momentive Performance Materials RTV6186 Clear Potting/Encapsulating Gel
- Multibase Multi-Flex® D 3104 TPO Thermoplastic Polyolefin Elastomer
- SABIC Innovative Plastics LNP THERMOCOMP 5C004 FP-V (PVDF)
- DuPont™ Nomex® 418 Paper, 10 mil Nominal Thickness
- ExxonMobil Label-Lyte® 440 LL-201 Matte Finish, Clear OPP Overlaminate
- Dow DNDB-1077 NT 7 Linear Low Density Polyethylene Resin
- DuPont Teijin Films Mylar® HR951 Polyester Film, 92 Gauge
- Chem Polymer Chemlon 130 GVH Nylon 66, 30% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved