Toyobo PELPRENE™ P40B Polyester TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo PELPRENE™ P40B Polyester TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Polyester TPEInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.56 % | 0.56 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.0040 cm/cm @Thickness 2.00 mm |
0.0040 in/in @Thickness 0.0787 in |
|
| Melt Index of Compound | 10 g/10 min @Temperature 190 °C |
10 g/10 min @Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 82 | 82 | JIS K6301 |
| Hardness, Shore D | 31 | 31 | ASTM D2240 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
| Elongation at Break | 820 % | 820 % | ASTM D638 |
| 50% Modulus | 0.00340 GPa | 0.493 ksi | ASTM D638 |
| Flexural Modulus | 0.0230 GPa | 3.34 ksi | ASTM D790 |
| Compressive Modulus | 0.00240 GPa | 0.348 ksi | 0.1; ASTM D695 |
| Resilience | 81 | 81 | JIS K6301 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tear Strength | 76.0 kN/m | 434 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 20 | 20 | ASTM D1044 |
| Compression Set | 49 % | 49 % | JIS K6301 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 200 µm/m-°C @Temperature 20.0 °C |
111 µin/in-°F @Temperature 68.0 °F |
TMA |
| Melting Point | 180 °C | 356 °F | By DSC |
| Vicat Softening Point | 89.0 °C | 192 °F | ASTM D1525 |
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | JIS K6301 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | JIS K2111 |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 BR80 Nylon 6.6 for injection molding, 80% bronze filled
- Ineos H02C-00 Polypropylene Homopolymer
- Teknor Apex APEX® 94-A0098C-50 Polyvinyl Chloride, Flexible
- SPHERE ONE EXTENDOSPHERESâ„¢ PM 6550 Hollow Plastic Spheres
- Tra-Con Tra-Bond FDA2 Food and Drug Application Epoxy Adhesive
- Plastics Group Polifil® GFPP-20 20% Glass-Reinforced Polypropylene
- Eastman Tenite Butyrate 264E0096908 Natural, Trsp Cellulose Acetate Butyrate
- Covestro Makrolon® 9417 Polycarbonate, 10% Glass Filled
- 3M FV090 Soft Translucent Vinyl Label Products
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR N220 (ISAF) Filler
Copyright © lookpolymers.com All Rights Reserved