Total PPR 8473 Polypropylene, Film Extrusion Grade
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Total Atofina |
| Trade Name | PPR |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Total PPR 8473 Polypropylene, Film Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Random copolymer heat sealable film gradeColor/Clarity/Impact - FINA 8473 is a low melting, high ethylene random copolymer with improved color, optics and impact properties.Heat Sealable - The very low melting point of FINA 8473 makes it an excellent heat seal layer for oriented films.Slip/Antiblock - FINA 8473 is available with custom slip and antiblock packages.FDA - FINA 8473 complies with all applicable FDA regulations Title 21 CFR Section 177.1520(c) 3.1 and may be used under these provisions for food contact and packaging.Recommended Applications - FINA 8473 is recommended for use in non- oriented film processes for manufacture of packaging films that require improved optical and impact properties and as a heat seal layer for oriented filmsProcessing - FINA 8473 resin processes on film extrusion equipment with typical melt temperatures of 390- 450°F (199-232°C).Data provided by the manufacturer, Total Petrochemicals.Total Petrochemicals acquired former Fina and Atofina plastics product lines.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Permeability | 14.0 g mil/ (m2 day) @Temperature 37.8 °C |
0.903 g mil/ (100 in2 day) @Temperature 100 °F |
90% RH; ASTM E96 |
| Density | 0.895 g/cc | 0.0323 lb/in³ | ASTM D1505 |
| Melt Flow | 4.6 g/10 min | 4.6 g/10 min | Conditions not specified; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 500 % | 500 % | Non-oriented film; ASTM D882 |
| Secant Modulus | 0.480 GPa | 69.6 ksi | 1% Secant Modulus; Non-oriented Film; ASTM D882 |
| Dart Drop | 9.40 g/micron | 239 g/mil | F<sub>50</sub>; ASTM D 1709 |
| Seal Strength | >= 200 g/25 mm | >= 200 g/in | at 135°C, 15 psi pressure and 1 sec. |
| Film Tensile Strength at Break, MD | 20.0 MPa | 2900 psi | Non-oriented film; ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 134 °C | 273 °F | DSC |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 % | 2.0 % | Non-oriented film; ASTM D1003 |
| Gloss | 85 % | 85 % | 45°; Non-oriented film; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 199 - 232 °C | 390 - 450 °F | film extrusion |
Users viewing this material also viewed the following:
- Momentive Performance Materials Siloprenâ„¢ LSR 2040 Liquid Silicone Rubber - General Purpose
- H.C. Starck Amperweld® 1701.39 K2 Chromium Carbide RIII
- Mitsui LUCANTâ„¢ HC-20 Synthetic Oil
- Techmer ES Plastiblend® PPS/F 0328
- Zircar Ceramics AL-25/1700 Alumina Insulation
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 287ºF Cure Temperature
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR N220 Filler
- Denka TH-11 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene
- DuPont Performance Polymers Sorona® 3030GV BK001 Polytrimethylene Terephthalate (PTT)
- BASF Ultramid® A3HG6 Balance 30% Glass Filled PA 66/610 (Dry)