Total PPC 9760 Polypropylene, Heterophasic Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Total Atofina
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total PPC 9760 Polypropylene, Heterophasic Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ATOFINA Propylene 9760 is heterophasic copolymer. PPC 9760 is characterized by improved stiffness, creep resistance and high impact resistance.
Physical Properties Metric English Comments
Bulk Density 0.525 g/cc
0.0190 lb/in³
ISO 1183
Density 0.905 g/cc
0.0327 lb/in³
ISO 1183
Melt Flow 25 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 25 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 83
83
ISO 2039-2
Tensile Strength, Yield 25.0 MPa
3630 psi
ISO 527-2
Elongation at Yield 6.5 %
6.5 %
ISO 527-2
Tensile Modulus 1.40 GPa
203 ksi
ISO 527-2
Flexural Modulus 1.30 GPa
189 ksi
ISO 527-2
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
ISO 179
5.00 kJ/m²

@Temperature -20.0 °C
 2.38 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179
>= 4.00 J/cm²
>= 19.0 ft-lb/in²
ISO 180
0.550 J/cm²

@Temperature -20.0 °C
 2.62 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
120°C per hour; ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 48.0 °C
118 °F
120°C per hour; ISO 75-2
Vicat Softening Point 70.0 °C
158 °F
50N-50°C per hour; ISO 306
140 °C
284 °F
10N-50°C per hour; ISO 306