Total PPC 1640 Polypropylene, Heterophasic Copolymer, Non-pressure Pipes

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Extrusion Grade
Manufacturer	Total Atofina
Trade Name	PPC
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total PPC 1640 Polypropylene, Heterophasic Copolymer, Non-pressure Pipes.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polypropylene PPC 1640 is a nucleated heterophasic (block) copolymer with a Melt Flow index of 0.3 g/10 min. This resin has a long-term heat stabilization package. It exhibits high stiffness in combination with outstanding impact strength even at very low temperatures.Polypropylene PPC 1640 has been specifically developed for the extrusion of non-pressure pipes. Other applications include sheet and blow molding.Information provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.905 g/cc	0.905 g/cc	ISO 1183
Bulk Density	0.525 g/cc	0.0190 lb/in³	ISO 1183
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 230 °C	0.30 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	28.0 MPa	4060 psi	ISO 527-2
Elongation at Yield	9.0 %	9.0 %	ISO 527-2
Tensile Modulus	1.34 GPa	194 ksi	ISO 527-2
Flexural Modulus	1.35 GPa	196 ksi	ISO 178
Izod Impact, Notched (ISO)	8.00 kJ/m² @Temperature -20.0 °C	3.81 ft-lb/in² @Temperature -4.00 °F	ISO 180
	>= 80.0 kJ/m² @Temperature 23.0 °C	>= 38.1 ft-lb/in² @Temperature 73.4 °F	ISO 180
Charpy Impact, Notched	0.800 J/cm² @Temperature -20.0 °C	3.81 ft-lb/in² @Temperature -4.00 °F	ISO 179
	>= 8.00 J/cm² @Temperature 23.0 °C	>= 38.1 ft-lb/in² @Temperature 73.4 °F	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	165 °C	329 °F	ISO 3146